Cost-effective activated carbons for CO₂ adsorption were developed from molasses using H₂SO₄, H₃PO₄, HCl, NaOH, and KOH as activating agents. At the temperature of 0 °C and a pressure of 1 bar, CO₂ adsorption equal to 5.18 mmol/g was achieved over activated carbon obtained by KOH activation. The excellent CO₂ adsorption of M-KOH can be attributed to its high microporosity. However, activated carbon prepared using HCl showed quite high CO₂ adsorption while having very low microporosity. The absence of acid species on the surface promotes CO₂ adsorption over M-HCl. The pore size ranges that are important for CO₂ adsorption at different temperatures were estimated. The higher the adsorption temperature, the more crucial smaller pores were. For 1 bar pressure and temperatures of 0, 10, 20, and 30 °C, the most important were pores equal and below: 0.733, 0.733, 0.679, and 0.536 nm, respectively.

Phase equilibria up to solidus line in CuO–In₂O₃ system have been investigated using XRD and DTA/TG methods. According to the results, only one compound of the formula Cu₂In₂O₅ formed in the system studied. Its thermal stability was determined in the air and argon proving that the compound did not melt but underwent decomposition. The decomposition of Cu₂In₂O₅ in the air atmosphere began at 1080 °C, while in argon at 835 °C. Additional studies were undertaken to determine the hitherto unknown colour properties of samples representing the CuO–In₂O₃ system in the equilibrium state.