We aimed to assess the crystallography, microstructure and flexural strength of zirconia-based ceramics made by stereolithography (SLA). Two additively manufactured 3 mol% yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP: LithaCon 3Y 230, Lithoz; 3D Mix zirconia, 3DCeram Sinto) and one alumina-toughened zirconia (ATZ: 3D Mix ATZ, 3DCeram Sinto) were compared to subtractively manufactured 3Y-TZP (control: LAVA Plus, 3M Oral Care). Crystallographic analysis was conducted by X-ray diffraction. Top surfaces and cross-sections of the subsurface microstructure were characterized using scanning electron microscopy (SEM). Biaxial flexural strength was statistically compared using Weibull analysis. The additively and subtractively manufactured zirconia grades revealed a similar phase composition. The residual porosity of the SLA 3Y-TZPs and ATZ was comparable to that of subtractively manufactured 3Y-TZP. Weibull analysis revealed that the additively manufactured LithaCon 3Y 230 (Lithoz) had a significantly lower biaxial flexural strength than 3D Mix ATZ (3D Ceram Sinto). The biaxial flexural strength of the subtractively manufactured LAVA Plus (3M Oral Care) was in between those of the additively manufactured 3Y-TZPs, with the additively manufactured ATZ significantly outperforming the subtractively manufactured 3Y-TZP. Additively manufactured 3Y-TZP showed comparable crystallography, microstructure and flexural strength as the subtractively manufactured zirconia, thus potentially being a good option for dental implants.

Titania (TiO₂) has attracted much attention recently for reducing bacterial diseases by the generation of reactive oxygen species (ROS) under UV irradiation. However, demand for higher photocatalytic activity due to higher recombination of electron and hole remains. The aims of this study were to make titania with higher antibacterial property and show the mechanisms of the bactericidal effect. In this study, we hydrothermally synthesized TiO₂ nanosheets (NS) with highly-oriented structures. Samples were divided into five groups, depending on the fluorine/titanium ratio in the raw material, namely NS1.0, NS1.2, NS1.5, NS1.8, and NS2.0. Facet ratio and nanosheet size increased with an increase of fluorine/titanium ratio. The photocatalytic activity of TiO₂ nanosheet was assessed by the generation of ROS. Hydroxyl radicals and superoxides were generated efficiently by ultraviolet light irradiation on NS1.5 and NS1.0, respectively. Antibacterial activity against Streptococcus mutans was assessed in the presence and absence of UV irradiation; NS1.0 showed superior antibacterial properties compared to commercially available TiO₂ nanoparticles, under both conditions, due to the oxidation of intracellular components and cell membrane. These results together suggested TiO₂ nanosheet induced bacterial cell death by oxidation, and TiO₂ facet engineering resulted in enhancement of both photocatalytic and antibacterial activities of TiO₂.

Messenger RNA (mRNA) is an emerging drug modality for protein replacement therapy. As mRNA efficiently provides protein expression in post-mitotic cells without the risk of insertional mutagenesis, direct delivery of mRNA can be applied, not only as an alternative to gene therapy, but also for various common diseases such as osteoarthritis (OA). In this study, using an mRNA-encoding interleukin-1 receptor antagonist (IL-1Ra), we attempted anti-inflammatory therapy in a rat model of the temporomandibular joint (TMJ) OA, which causes long-lasting joint pain with chronic inflammation. For the intra-articular injection of mRNA, a polyplex nanomicelle, our original polymer-based carrier, was used to offer the advantage of excellent tissue penetration with few immunogenic responses. While the protein expression was transient, a single administration of IL-1Ra mRNA provided sustained pain relief and an inhibitory effect on OA progression for 4 weeks. The mRNA-loaded nanomicelles provided the encoded protein diffusely in the disc and articular cartilage without upregulation of the expression levels of the pro-inflammatory cytokines IL-6 and tumor necrosis factor-α (TNF-α). This proof-of-concept study demonstrates how anti-inflammatory proteins delivered by mRNA delivery using a polyplex nanomicelle could act to alleviate OA, stimulating the development of mRNA therapeutics.

The effects of Ti, Nb, Ta, Zr, and Ag on cellular and bacterial adhesion were investigated in this study. Moreover, the relationships between surface compositions, metal ion release behaviors, and biological responses were examined. As a result, MC3T3-E1 cells and S. aureus were able to better attach to Ti and Zr rather than the Nb and Ta specimens. For the Ag specimen, the amount of Ag ions released into Hanks’ solution was the largest among all the specimens. Cellular and bacterial adhesion onto the Ag specimen was inhibited compared with the other specimens, because of Ag ion release. Alternatively, Nb and Ta specimens exhibited specific biological responses. Cellular adhesion on Nb and Ta specimens was similar to that on Ti, while bacterial adhesion on Nb and Ta specimens was inhibited compared with that on Ti. This study proved that Nb and Ta inhibited bacterial adhesion and exhibited no harmful effects on cellular adhesion. In addition, these results indicate that the passive layer on Nb and Ta plays a key role in the inhibition of bacterial adhesion.

Recently, silver (Ag) and copper (Cu) have been incorporated into a titanium (Ti) surface to realize their antibacterial property. This study investigated both the durability of the antibacterial effect and the surface change of the Ag- and Cu-incorporated porous titanium dioxide (TiO₂) layer. Ag- and Cu-incorporated TiO₂ layers were formed by micro-arc oxidation (MAO) treatment using the electrolyte with Ag and Cu ions. Ag- and Cu-incorporated specimens were incubated in saline during a period of 0–28 days. The changes in both the concentrations and chemical states of the Ag and Cu were characterized using X-ray photoelectron spectroscopy (XPS). The durability of the antibacterial effects against Escherichia coli (E. coli) were evaluated by the international organization for standardization (ISO) method. As a result, the Ag- and Cu-incorporated porous TiO₂ layers were formed on a Ti surface by MAO. The chemical state of Ag changed from Ag₂O to metallic Ag, whilst that of Cu did not change by incubation in saline for up to 28 days. Cu existed as a stable Cu₂O compound in the TiO₂ layer during the 28 days of incubation in saline. The concentrations of Ag and Cu were dramatically decreased by incubation for up to 7 days, and remained a slight amount until 28 days. The antibacterial effect of Ag-incorporated specimens diminished, and that of Cu was maintained even after incubation in saline. Our study suggests the importance of the time-transient effects of Ag and Cu on develop their antibacterial effects.