A series of Zn-modified HBeta (Zn/HBeta) catalysts were prepared via the wetness impregnation method with different zinc precursors such as ZnSO₄·7H₂O, ZnCl₂, C₄H₆O₄Zn·2H₂O and Zn(NO₃)₂·6H₂O, and their catalytic performance in the conversion of ethanol to propylene reaction was evaluated. Results indicate that the amount and strength distribution of the acid sites of the Zn/HBeta catalysts were easily tuned by employing different types of zinc precursors. More importantly, when the zinc species were introduced to the HBeta, the propylene yield was significantly enhanced, whereas the yields of ethylene and C₂–C₄ alkanes were remarkably suppressed. For the catalyst prepared by using the ZnCl₂ precursor, a higher propylene yield of up to 43.4% for Zn/HBeta-C was achieved as a result of the moderate amount and strength distribution of acid sites. The average coking rate of the used Zn/HBeta catalysts strongly depended on the amount of total acid sites, especially the strong acid sites, i.e., the higher the amount of total acid sites of the catalyst, the greater the average coking rate. For the catalyst prepared by using the ZnSO₄·7H₂O precursor, Zn/HBeta-S exhibited a better stability even after depositing more coke, which was due to the higher amount of strong acid sites.

A series of Zn-modified Hβ (Zn/Hβ) catalysts were prepared by using the different zinc precursors such as ZnSO4·7H2O, ZnCl2, C4H6O4Zn·2H2O and Zn(NO3)2·6H2O, and their catalytic performance in the ethanol conversion to propylene reaction was evaluated. Results indicate the amount and strength distribution of acid sites of the Zn/Hβ catalysts were easily tuned by employing different type of zinc precursors. More importantly, when the Zn species were introduced to the Hβ, the propylene yield was significantly enhanced, whereas the yields of the byproducts such as ethylene and C2-C4 alkanes were remarkably suppressed. For the catalyst prepared by using the ZnCl2 precursor (Zn/Hβ-C), a higher propylene yield up to 43.4% was achieved as a result of the moderate amount and distribution of acid sites. The average coking rate of the used Zn/Hβ catalysts strongly depended on the amount of total acid sites, especially the strong acid sites, i.e., the higher the amount of total acid sites of the catalyst, the greater the average coking rate. For the catalyst prepared by using the ZnSO4·7H2O precursor, Zn/Hβ-S exhibited a better stability even after depositing more coke, which is due to the higher amount of strong acid sites.

To overcome the inherent drawbacks of poly(propylene carbonate) (PPC), such as poor thermal stability, low mechanical strength, and high surface energy, this study introduced, for the first time, 1,1,1-trifluoro-2,3-epoxypropane (TF-PO) as a third monomer into the metal-free TEB/PPNCl catalytic system for the terpolymerization with carbon dioxide (CO₂) and propylene oxide (PO), successfully synthesizing a series of fluorinated PPC (PPCF). The optimal polymerization conditions ($60 °C$, 2.0 MPa, 12 h, n(PO):n(TF-PO) = 100:4) were determined through systematic optimization. Comprehensive structural characterization (FT-IR, NMR, XPS) confirmed the successful incorporation of TF-PO into the polymer backbone. Property evaluation revealed that the PPCF materials exhibited substantial improvements in thermal stability, mechanical strength, hydrophobicity, and dielectric properties compared to unmodified PPC. The optimal sample, PPCF4, achieved a $5\%$ weight-loss temperature ($T_{d,-5\%}$) of $242 °C$, a glass transition temperature ($T_{\mathrm{g}}$) of $42 °C$, a tensile strength of 21.5 MPa, and a Young modulus of 296 MPa. With a $5\%$ TF-PO feed ratio, the material’s water contact angle increased to 102°, and its dielectric constant reached 6.01 at ${10}^4$ Hz. Furthermore, density functional theory (DFT) calculations elucidated the Lewis acidity of the TEB catalyst and the reactive sites of the monomers, leading to a proposed mechanism for the ternary alternating copolymerization. This work provides an effective synthetic strategy and theoretical foundation for preparing high-performance and functionalized PPC materials through molecular structure design.