This paper presents the results of studies of the nanoporous silicon structure, both with different pore depths (up to 180 μm) and with layers in which a graphene-like coating was synthesized on the inner surface of the pores. The nanoporous layers were characterized by SEM as well as IR and Raman spectroscopy. Cyclic voltammetry and galvanostatic charge–discharge data in 3 M H₂SO₄ are presented as well as the results of the cyclic stability of these characteristics for the nanoporous structure. It was found that the degree of electrolyte pre-impregnation significantly affected the electrochemical processes, and the capacitance values depended on the depth (thickness) of the nanoporous layer. Increasing the thickness of the porous layer led to an increase in area-normalized pseudocapacity and was limited only by the mechanical strength of the structure. Performance improvement was also achieved by synthesis of the graphene-like layer in the volume of the nanoporous structure. The electrodes (composite materials) proposed in the work showed one of the best capacitive characteristics (87 mF/cm² with 100% capacity retention after 15,000 cycles) in comparison with the data reported in the literature at present.

This work presents a method for preparing an Fe₂O₃/MWCNT/Al composite electrode without the use of a binder. Synthesizing the composite material directly on conductive substrates allows one to obtain ready-made supercapacitor electrodes characterized by high values of specific capacity, as well as resistance to numerous charge/discharge cycles. Using an array of multi-walled carbon nanotubes (MWCNTs) as a conductive base for the synthesis of iron oxide allows for the production of a composite material that combines the positive properties of both materials. The Fe₂O₃/MWCNT/Al composite was formed using electrochemical oxidation of the MWCNT/Al material in a mixture of 0.1 M aqueous solution of Fe(NH₄)₂(SO₄)₂ (iron ammonium sulfate) and 0.08 M CH₃COONa (sodium acetate) in a 1:1 ratio. The proposed approaches to fabricating composite electrodes provide excellent performance characteristics, namely high cyclic stability and fast response time. For the first time, an Fe₂O₃/MWCNT/Al composite was obtained using electrochemical oxidation of Fe²⁺ on the surface of MWCNTs grown directly on aluminum foil. The specific capacitance of the obtained composite material reaches 175 F/g at a scanning rate of 100 mV/s. The capacity loss during cyclic measurements does not exceed 25% after 10,000 charge/discharge cycles.

Resistive random-access memory (RRAM) is a crucial element for next-generation large-scale memory arrays, analogue neuromorphic computing and energy-efficient System-on-Chip applications. For these applications, RRAM elements are arranged into Crossbar arrays, where rectifying selector devices are required for correct read operation of the memory cells. One of the key advantages of RRAM is its high scalability due to the filamentary mechanism of resistive switching, as the cell conductivity is not dependent on the cell area. Thus, a selector device becomes a limiting factor in Crossbar arrays in terms of scalability, as its area exceeds the minimal possible area of an RRAM cell. We propose a tunnel diode selector, which is self-aligned with an RRAM cell and, thus, occupies the same area. In this study, we address the theoretical and modeling aspects of creating a self-aligned selector with optimal parameters to avoid any deterioration of RRAM cell performance. We investigate the possibilities of using a tunnel diode based on single- and double-layer dielectrics and determine their optimal physical properties to be used in an HfOx-based RRAM Crossbar array.

In this work, a method has been developed for the to prepare a Fe2O3/MWCNT/Al composite electrode without the use of a binder. The synthesis of the compo-site material directly on conductive substrates allows to obtain ready-made supercapacitor elec-trodes characterised by high values of specific capacity as well as resistance to numerous charge/discharge cycles. The use of an array of multi-walled carbon nanotubes (MWCNTs) as a conductive base for the synthesis of iron oxide allows the production of a composite material that combines the positive properties of both materials. The Fe2O3/MWCNT/Al composite was formed by electrochemical oxidation of the MWCNT/Al material in a mixture of 0.1 M aqueous solution of Fe(NH4)2(SO4)2 ( iron ammonium sulfate) and 0.08 M CH3COONa (sodium acetate) in a 1:1 ratio. The proposed approaches to fabricate composite electrodes provide excellent performance characteristics: excellent cyclic stabil-ity and high response time. For the first time, the Fe2O3/MWCNT/Al composite was obtained by electrochemical oxidation of Fe2+ on the surface of MWCNTs grown directly on aluminum foil. The specific capacitance of the obtained composite material reaches 175 F/g at a scanning rate of 100 mV/s. The capacity loss during cyclic measurements does not exceed 25% after 10,000 charge/discharge cycles.