In this study, the structural and electrical properties of orthorhombic κ-Ga₂O₃ films prepared using Halide Vapor Phase Epitaxy (HVPE) on AlN/Si and GaN/sapphire templates were studied. For κ-Ga₂O₃/AlN/Si structures, the formation of two-dimensional hole layers in the Ga₂O₃ was studied and, based on theoretical calculations, was explained by the impact of the difference in the spontaneous polarizations of κ-Ga₂O₃ and AlN. Structural studies indicated that in the thickest κ-Ga₂O₃/GaN/sapphire layer used, the formation of rotational nanodomains was suppressed. For thick (23 μm and 86 μm) κ-Ga₂O₃ films grown on GaN/sapphire, the good rectifying characteristics of Ni Schottky diodes were observed. In addition, deep trap spectra and electron beam-induced current measurements were performed for the first time in this polytype. These experiments show that the uppermost 2 µm layer of the grown films contains a high density of rather deep electron traps near E_c − 0.3 eV and E_c − 0.7 eV, whose presence results in the relatively high series resistance of the structures. The diffusion length of the excess charge carriers was measured for the first time in κ-Ga₂O₃. The film with the greatest thickness of 86 μm was irradiated with protons and the carrier removal rate was about 10 cm⁻¹, which is considerably lower than that for β-Ga₂O₃.

ZnO nanorods are promising materials for many applications, in particular for UV detectors. In the present paper, the properties of high crystal quality individual ZnO nanorods and nanorod arrays grown by the self-catalytic CVD method have been investigated to assess their possible applicationsfor UV photodetectors. X-ray diffraction, Raman spectroscopy and cathodoluminescence investigations demonstrate the high quality of nanorods. The nanorod resistivity and carrier concentration in dark is estimated. The transient photocurrent response of both as grown and annealed at 550 °C nanorod array under UV illumination pulses is studied. It is shown that annealing increases the sensitivity and decreases the responsivity that is explained by oxygen out-diffusion and the formation of near surface layer enriched with oxygen vacancies. Oxygen vacancy formation due to annealing is confirmed by an increase of green emission band intensity.

An original technique of chemical deposition (CVD) by catalytic pyrolysis of ethanol vapor was used to directly grow multiwall carbon nanotubes (MWCNTs) layers on aluminum foil. The grown nanotubes had excellent adhesion and direct electrical contact to the aluminum substrate. This material was perfect for use in electrochemical supercapacitors. In this work, the possibility of a significant increase in the specific capacity of MWCNTs by simple electrochemical oxidation was investigated. The optimal conditions for improving the characteristics of the MWCNT/Al electrodes were found. Electrochemical treatment of MWCNT/Al electrodes in a 0.005 M Na₂SO₄ solution at a potential of 4–5 V for 20–30 min increased the specific capacity of MWCNTs from 30 F/g to 140 F/g. The properties of modified nanotubes were investigated by X-ray photoelectron spectroscopy, cyclic voltammetry (CV), and impedance spectroscopy. A significant increase in the concentration of oxygen-containing functional groups on the surface of MWCNTs was found as a result of electrochemical oxidation. The modified MWCNT/Al electrodes maintained excellent stability to multiple charge–discharge cycles. After 20,000 CVs, the capacity loss was less than 5%. Thus, the results obtained significantly expanded the possibilities of using MWCNT/Al composite materials obtained by the method of direct deposition of carbon nanotubes on aluminum foil as electrodes for supercapacitors.

Zinc oxide is a promising material for the creation of various types of sensors, in particular UV detectors. In this work, arrays of ordered nanorods were grown by chemical vapor deposition. The effect of environmental humidity on the sensing properties of zinc oxide nanorod arrays was investigated, and a prototype UV sensor using indium as an ohmic contact was developed. UV photoresponses were measured for the samples stored in dry and wet atmospheres. The increase in sensitivity and response of the ZnO nanorod arrays was observed after prolonged exposure to a wet atmosphere. A model was proposed to explain this effect. This is due to the formation of hydroxyl groups on the surface of zinc oxide nanorods, which is confirmed by FTIR spectroscopy data. For the first time, it has been shown that after storage in a wet atmosphere, the sensory properties of the structure remain stable regardless of the ambient humidity.

Recently, significant progress has been made in the performance of supercapacitors through the development of composite electrodes that combine various charge storage mechanisms. A new method for preparing composite binder-free MnO₂/MWCNT/Al electrodes for supercapacitors is proposed. The method is based on the original technique of direct growth of layers of multi-walled carbon nanotubes (MWCNTs) on aluminum foil by the catalytic pyrolysis of ethanol vapor. Binder-free MnO₂/MWCNT/Al electrodes for electrochemical supercapacitors were obtained by simply treating MWCNT/Al samples with an aqueous solution of KMnO₄ under mild conditions. The optimal conditions for the preparation of MnO₂/MWCNT/Al electrodes were found. The treatment of MWCNT/Al samples in a 1% KMnO₄ aqueous solution for 40 min increased the specific capacitance of the active material of the samples by a factor of 3, up to 100–120 F/g. At the same time, excellent adhesion and electrical contact of the working material to the aluminum substrate were maintained. The properties of the MnO₂/MWCNT/Al samples were studied by electron probe microanalysis (EPMA), Raman spectroscopy, cyclic voltammetry (CV), and impedance spectroscopy. Excellent charge/discharge characteristics of composite electrodes were demonstrated. The obtained MnO₂/MWCNT/Al electrodes maintained excellent stability to multiple charge-discharge cycles. After 60,000 CVs, the capacitance loss was less than 20%. Thus, this work opens up new possibilities for using the MWCNT/Al material obtained by direct deposition of carbon nanotubes on aluminum foil for the fabrication of composite binder-free electrodes of supercapacitors.

The effect of the length of ZnO nanorods on the mode structure and thresholds of stimulated and laser luminescence in the ultraviolet spectral region is studied. It is shown that nanorods with a metal mirror at the end face exhibit the minimum optical excitation power threshold in the case of long nanoresonators. Single-mode lasing is observed in short ZnO nanorods. Variations in the lasing thresholds are attributed to differences in the length of the amplifying medium and in the local densities of photon states in regularly shaped nanocrystals.