The transformation of kaolinite into metakaolinite by thermal activation to obtain highly active aluminosilicate is commonly known. In addition to kaolin, the high content of kaolinite in coal mining waste is another potential source for obtaining an aluminosilicate precursor, thereby protecting the environment and adding value to industrial wastes. In this paper, the kaolinite-based high ash slime (KAS) was calcined at temperatures ranging from 400 °C to 1000 °C under air, N₂, and CO₂ atmospheres, respectively. The thermal behaviors and structural evolution of each component in KAS were analyzed by thermal analysis (TG-DSC), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS). Moreover, the chemical reactivity of Al₂O₃ and SiO₂ in calcined KAS was evaluated by HCl and NaOH leaching methods. The results show that the applied KAS in this study primarily consisted of kaolinite and carbon, while the minor mineral phases included quartz, calcite, and pyrite. Additionally, the structural transformation of kaolinite during calcination included dehydroxylation, sintering, and the formation of mullite. Crystalline kaolinite completely decomposed into semicrystalline metakaolinite at 600–800 °C, accounting for the increase in chemical reactivity. The interlayer sintering of metakaolinite and the recrystallization of amorphous components led to the decrease in chemical reactivity after 800 °C. Furthermore, the thermal behaviors of carbon in KAS are greatly affected by the calcination atmosphere. The presence of carbon reduced the chemical reactivity of calcined KAS.

The cleaning process of coals is challenging due to the existence of clay minerals. The overall objective of this study is to investigate how the dewatering of coal slurry is impacted by the presence of clay minerals, i.e., kaolinite and montmorillonite. Filtration tests were first conducted to investigate the effect of kaolinite and montmorillonite on the dewatering efficiency of coal. Specifically, we measured the filtration velocity, moisture, average specific resistance, and porosity of filter cakes for six slurry samples, in which different amounts of kaolinite and montmorillonite were contained. Filtration tests show that a small amount of kaolinite and montmorillonite leads to a significant reduction in the filtration velocity and porosity, and a big increase in the average specific resistance and the moisture of the filter cake. We observe that most kaolinite existed in the top and middle layers of the filter cake, while most montmorillonite existed in the top layer; on the contrary, little montmorillonite is observed in the middle and bottom layers of the filter cake. Montmorillonite results in a much more deteriorative effect than kaolinite. Considering that the interactions between clay minerals and water may play a key role, we then further investigate the effect of such interactions using molecular simulations. Simulation results show that water molecules could hardly diffuse into kaolinite from the edge, while they could readily penetrate into the montmorillonite layers from the edge surface. This result can be explained by the hydrated cation in montmorillonite. The adsorption density of water on the octahedral surface of kaolinite is higher than that of water on the tetrahedral surface of kaolinite. Furthermore, the adsorption density of water on the double surfaces of kaolinite is higher than that of water on the montmorillonite surface. This research is expected to provide benefits or contributions to the dewatering of clay-rich coal tailings.

High-ash coal, also known as low-grade coal, has becomes a viable alternative in recent years to high-quality coal because available resources have become increasingly scarce due to extensive mining activity. This work aims to provide a comprehensive understanding of the structural characteristics of high-ash coal and construct a plausible molecular structure to elucidate its chemical reactivity in future applications. Its properties were investigated using Solid-state ¹³C nuclear magnetic resonance (¹³C NMR), X-ray photoelectron spectroscopy analysis (XPS), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR). The molecular structure was constructed and validated using Material Studio, LAMMPS Software Package, and MATLAB program. The characterization results revealed that high-ash coal contains 72.15% aromatic carbon, significantly surpassing the percentage of aliphatic carbon (27.85%). The ratio of bridgehead carbon to peripheral aromatic carbon was calculated as 0.67, indicating that the pentacene is the main carbon skeleton form in the high-ash coal structure. Furthermore, oxygen-containing functional groups presented as C=O/O–C–O, C–O, and COO– within the structure along with pyridine and pyrrolic structures. Consequently, the molecular structure comprises pentacene with aliphatic carbon chains, such as methylene, that connect the benzene rings and form a three-dimensional network. The results of a simulated IR spectrum and contact angle simulation aligned with the experimental results, validating the molecular structure of high-ash coal. The chemical formula for the high-ash coal model was determined as C₂₀₃H₁₈₉N₇O₆₁S with a molecular weight of 3734.79.

The preparation of an environmentally friendly and efficient flocculant for solid-liquid separation in industrial wastewater is highly important. In this study, a novel cationic flocculant (AL-g-PAMA) was synthesized by a thermal initiation method using alkali lignin (AL) as the main chain and acrylamide (AM) and methacrylamido propyl trimethyl ammonium chloride (MAPTAC) as the grafted side chains. The structure, thermal stability, and surface morphology of the copolymers were investigated by various characterization methods. The results indicated the successful synthesis of AL-g-PAMA. AL-g-PAMA was applied to improve solid-liquid separation in kaolin suspensions. The results showed that AL-g-PAMA had excellent flocculation-sedimentation and dewatering efficiency. When the dosage of AL-g-PAMA #5 was 600.0 g/t_(s), the thickness of the compressed layer was 2.2 cm, the floc settling velocity was 24.1 cm/min, and the transmittance of the supernatant was 84.0%. The moisture content of the filter cake decreased from 55.0% to 43.4% after treatment with AL-g-PAMA #5. The results of zeta potential and focused beam reflectance measurement (FBRM) analysis indicated that bridging and electroneutralization were the main flocculation mechanisms. Therefore, this study extends the potential for using lignin as a bioflocculant and provides a feasible approach to efficiently purify high-turbidity wastewater.