To enhance the damage resistance of protective engineering materials under extreme loads such as explosions and impacts, this study, building upon the improvement in impact resistance of concrete achieved by rubber modification, further incorporates steel fibers and glass fibers to synergistically enhance impact resistance and to investigate the underlying mechanisms. Using split Hopkinson pressure bar (SHPB) testing, a comparative investigation was conducted on the dynamic mechanical responses of four specimen groups, namely plain rubberized concrete, single steel fiber-reinforced, single glass fiber-reinforced, and hybrid steel–glass fiber-reinforced rubberized concrete, over a strain-rate range of 30–185 s⁻¹. The results demonstrate that the incorporation of hybrid fibers significantly enhances the dynamic compressive performance of plain rubber concrete. Specifically, the dynamic compressive strength increases from 40.73–61.29 MPa to 60.25–101.86 MPa, accompanied by a 59.5% increase in strain-rate sensitivity. Meanwhile, the fragment fineness modulus after failure rises from 3.20–3.33 to 3.73–4.20, indicating improved post-impact integrity. In addition, the hybrid fiber-reinforced specimens exhibit the highest energy dissipation capacity at identical strain rates. Their dynamic stress–strain responses are characterized by higher stiffness, improved ductility, and more pronounced progressive failure behavior. These findings provide experimental evidence for the design of high-impact-resistant protective engineering materials.

As an environmentally friendly construction material, recycled rubber concrete (RRC) is commonly used as a road material owing to its excellent flexural strength and crack resistance. Previous studies have shown that the addition of fibres is an effective method for improving the crack resistance of concrete. The purpose of this study is to investigate the fracture performance of RRC reinforced with steel fibres (SFs) and glass fibres (GFs). A total of 28 RRC mixtures were prepared. The results of the fracture test showed that the addition of SFs and GFs significantly enhanced the RRC fracture performance. The maximum increases or decreases in flexural strength, brittleness coefficient, fracture energy, initial fracture toughness, and unstable fracture toughness were 64.9, −34.6, 775.6, 92.0, and 118.4%, respectively. The ideal GF content is usually in the range of 0.4–0.6% and decreases with increasing SF content. In addition, scanning electron microscope (SEM) tests were conducted to explore the mechanism of the effect of hybrid fibres on RRC at a microscopic level. The results show that SFs were always pulled out, while GFs were pulled apart at the initial defects. At the same time, excessive GFs caused more initial defects. These results are expected to provide theoretical direction and experimental support for the practical application of hybrid fibre-reinforced recycled rubber concrete (HFRRRC).