Dissimilar welds between ferritic and austenitic steels represent a good solution for exploiting the best performance of stainless steels at high and low temperatures and in aggressive environments, while minimizing costs. Therefore, they are widely used in nuclear and petrochemical plants; however, due to the different properties of the steels involved, the welding process can be challenging. Fusion welding can be specifically applied to connect low-carbon or low-alloy steels with high-alloy steels, which have similar melting points. The welding of thick plates can be performed with an electric arc in multiple passes or in a single pass by means of laser beam equipment. Since the microstructure and, consequently, the mechanical properties of the weld are closely related to the composition, the choice of the filler metal and processing parameters, which in turn affect the dilution rate, plays a fundamental role. Numerous technical solutions have been proposed for welding dissimilar steels and much research has developed on welding metallurgy; therefore, this article is aimed at a review of the most recent scientific literature on issues relating to the fusion welding of ferritic/austenitic steels. Two specific sections are dedicated, respectively, to electric arc and laser beam welding; finally, metallurgical issues, related to dilution and thermal field are debated in the discussion section.

Carbon and low-alloy steel plates clad with stainless steel or other metals are a good choice to meet the demand for cost-effective materials to be used in many corrosive environments. Numerous technical solutions are developed for the production of clad steel plates, as well as for their joining by fusion welding. For thick plates, a careful strategy is required in carrying out the multiple passes and in choosing the most suitable filler metals, having to take into account the composition of the base metal and the cladding layer. The specificity of the different processes and materials involved requires an adequate approach in the study of the metallurgical characteristics of clad steel, thus arousing the interest of researchers. Focusing mainly on ferritic steel plates clad with austenitic steel, this article aims to review the scientific literature of recent years which deals with both the production and the fusion welding processes. The metallurgical issues concerning the interfaces and the effects of microstructural characteristics on mechanical behaviour and corrosion resistance will be addressed; in particular, the effects on the fusion and thermally affected zones that form during the fusion welding and weld overlay processes will be analysed and discussed.

An integrated experimental-theoretical approach to the metallurgical characterization of the interfaces in steel plates clad by hot rolling is proposed. Three different couplings of materials have been studied: ASTM A 515 Gr.60 low carbon steel clad with austenitic stainless steel AISI 304L; extra low carbon steel ASTM A283 clad with high Ni content Alloy 59; and, low carbon steel AISI 1010 clad with Cu-Ni Monel 400. Experimental investigations, which are addressed to analyse the microstructural changes near the interfaces and identify the present phases, have been carried out through scanning electron microscopy (SEM) observations, microanalytical measurements by energy dispersive spectroscopy (EDS), and Vickers microhardness tests. In all of the cases examined, the zones that are affected by detrimental microstructural changes results in being considerably less thick than the overall cladding layer. Simulations that are based on theoretical diffusion modelling have been integrated to the experimental characterization by introducing a cladding parameter that acts on the diffusion bonding efficiency, in order to evaluate the effects of process temperature and time variations on diffusion bonding efficiency and stability. In particular, this analytical investigation has shown how the shorter is the duration of the diffusion transient and the higher the temperature, the lower results the sensitivity of the diffusion processes to temperature fluctuations.

Dissimilar welds between ferritic and austenitic steels represent a good solution for exploiting the best performance of stainless steels at high and low temperatures and in aggressive environments, while minimizing costs. Therefore, they are widely used in nuclear and petrochemical plants, however, due to the different properties of the steels involved, the welding process can be challenging. Fusion welding can be specifically addressed to connect low-carbon, or low-alloy steels, with high-alloy steels, which have similar melting point. Welding of thick plates can be performed with electric arc in multiple passes or in a single pass by means of a laser beam equipment. Since microstructure and consequently mechanical properties of the weld are closely related to composition, the choice of the filler metal and processing parameters, which in turn affects the dilution rate, plays a fundamental role. Numerous technical solutions were proposed for welding dissimilar steels and much research was developed on the weldment metallurgy; therefore, this article is aimed at a review of the most recent scientific literature on the issues relating to the fusion welding of ferritic / austenitic steels. Two specific sections are dedicated respectively to electric arc and laser beam welding; finally, metallurgical issues, related to dilution and thermal field are debated in the discussion section.

Over the past 20 years, laser beam–electric arc hybrid welding has gained popularity, enabling high quality and efficiency standards needed for steel welds in structures subjected to severe working conditions. This process enables single-pass welding of thick components, overcoming issues concerning the individual use of traditional processes based on an electric arc or laser beam. Therefore, thorough knowledge of both processes is necessary to combine them optimally in terms of efficiency, reduced presence of defects, corrosion resistance, and mechanical and metallurgical features of the welds. This article aims to review the technical and metallurgical aspects of hybrid welding reported in the scientific literature mainly of the last decade, outlining possible choices for system configuration, the inter-distance between the two heat sources, as well as the key process parameters, considering their effects on the weld characteristics and also taking into account the consequences for solidification modes and weld composition. Finally, a specific section has been reserved for hybrid welding of clad steel plates.