Thanks to their excellent mechanical strength in combination with low density, high melting point, and good resistance to corrosion, titanium alloys are very useful in many industrial and biomedical fields. The new additive manufacturing methods, such as Electron Beam Powder Bed Fusion based on the deposition of metal powders layers progressively molten by electron beam scanning, can overcome many of the machining problems concerning the production of peculiar shapes made of Ti alloys. However, the processing route is strictly determinant for mechanical performance of products, especially in the case of Ti alloys. In the present work flat specimens made of Ti-6Al-4V alloy produced by Electron Beam Powder Bed Fusion (or Electron Beam Melting) have been built and post-processed with the purpose of obtaining good tensile and creep performance. Preliminarily, the process parameters were set according to literature evidence and machine producer recommendations, validated by the results of a thermal analysis, aimed at satisfying the best processing conditions to reduce defects, as unmelted regions, microstructure coarsening or porosity, that are detrimental to mechanical behavior. Subsequently, Hot Isostatic Pressing and surface smoothing were considered, respectively, in order to reduce any internal porosity and lower roughness. Microstructure of the investigated specimens was characterized by optical and scanning electron microscopy observations and by X-ray diffraction measurements. Results show enhanced tensile behavior after the hot pressing treatment that allows to relieve stresses and reduce defects detrimental to mechanical properties. The best ductility was obtained by the combined effects of machining and densification. Creep test results verify the beneficial effects of surface smoothing.

Dissimilar welds between ferritic and austenitic steels represent a good solution for exploiting the best performance of stainless steels at high and low temperatures and in aggressive environments, while minimizing costs. Therefore, they are widely used in nuclear and petrochemical plants; however, due to the different properties of the steels involved, the welding process can be challenging. Fusion welding can be specifically applied to connect low-carbon or low-alloy steels with high-alloy steels, which have similar melting points. The welding of thick plates can be performed with an electric arc in multiple passes or in a single pass by means of laser beam equipment. Since the microstructure and, consequently, the mechanical properties of the weld are closely related to the composition, the choice of the filler metal and processing parameters, which in turn affect the dilution rate, plays a fundamental role. Numerous technical solutions have been proposed for welding dissimilar steels and much research has developed on welding metallurgy; therefore, this article is aimed at a review of the most recent scientific literature on issues relating to the fusion welding of ferritic/austenitic steels. Two specific sections are dedicated, respectively, to electric arc and laser beam welding; finally, metallurgical issues, related to dilution and thermal field are debated in the discussion section.

Carbon and low-alloy steel plates clad with stainless steel or other metals are a good choice to meet the demand for cost-effective materials to be used in many corrosive environments. Numerous technical solutions are developed for the production of clad steel plates, as well as for their joining by fusion welding. For thick plates, a careful strategy is required in carrying out the multiple passes and in choosing the most suitable filler metals, having to take into account the composition of the base metal and the cladding layer. The specificity of the different processes and materials involved requires an adequate approach in the study of the metallurgical characteristics of clad steel, thus arousing the interest of researchers. Focusing mainly on ferritic steel plates clad with austenitic steel, this article aims to review the scientific literature of recent years which deals with both the production and the fusion welding processes. The metallurgical issues concerning the interfaces and the effects of microstructural characteristics on mechanical behaviour and corrosion resistance will be addressed; in particular, the effects on the fusion and thermally affected zones that form during the fusion welding and weld overlay processes will be analysed and discussed.