In this study, lychee (Litchi chinensis Sonn.) pericarp powder was added to chitosan (CHS) matrix to develop active packaging films, and their structure, physicochemical, antibacterial, antioxidant, and functional properties were investigated. FT-IR results showed that intermolecular hydrogen bonds were formed between CHS and polyphenols in lychee pericarp powder (LPP), and the intermolecular interaction interfered with the assembly of CHS into semi-crystal structure, which reduced the crystallinity of CHS film. Incorporation of LPP significantly reduced water vapor permeability, water solubility, swelling degree, and elongation at break of CHS film (p < 0.05). However, UV-visible light barrier, tensile strength, and antibacterial and antioxidant properties of CHS films were increased by LPP incorporation. CHS-LPP film remarkably lowered the weight loss, firmness, titratable acidity, and total soluble solids of fresh-cut apple after five days storage. CHS-LPP film packaging effectively inhibited the browning of fresh-cut apple and the reduction of polyphenol content in apple juice caused by polyphenol oxidase (PPO)-mediated oxidation during storage. Therefore, CHS-LPP films have great potential as food packaging material to ensure the quality and extend the shelf life of food products.

Plasticizers and the water migration of edible protein films during storage can result in changes in film properties, while specific changing processes need to be further explored. In this study, glycerol-plasticized soy protein isolate (SPI) films were stored at 25 °C, 4 °C, and −18 °C for 6 weeks (relative humidity (RH), 40–50%). The glycerol migration was monitored by the glycerol migration rate and differential scanning calorimetry (DSC). Water content, low-field nuclear magnetic resonance (LF-NMR), and thermogravimetric analysis (TGA) were used to analyze the water state. The results showed that significant pores and cracks were observed after storage at 25 °C. The proportion of bound water gradually increased, and the glycerol migration rate also reached 1.3% and 0.7% at 25 °C and 4 °C, respectively. The results proved that increasing the storage temperature accelerated the loss of water and glycerol, and decreased the mechanical properties of the SPI film.