The presented work offers an innovative process scheme for valorizing Pb-Zn slag, which involves crushing, grinding, and separation techniques to concentrate valuable components (non-ferrous metals). This methodology could have a significant impact on the global beneficiation of metallurgical slags since it is significantly more simple, environmentally friendly, and cost-effective than standard pyro- and hydrometallurgical procedures. According to previous physicochemical and mineralogical studies, Pb-Zn slag is a valuable secondary raw material. This inhomogeneous technogenic resource contains substantial amounts of non-ferrous metals (Pb, Zn, Cu, and Ag). However, laboratory tests have indicated that the Pb-Zn slag contains highly uneven amounts of valuable metals, ranging from several g/ton to tens of g/ton. The main issue is that traditional metallurgical procedures for releasing beneficial elements are not commercially viable since the elements are “trapped” within the amorphous aluminosilicates or intergrowths of alloy grains and glassy phases. Gravity concentration (Wilfley 13 shaking table) and magnetic separation (Davis separator and disk separator) were used to obtain the final concentrate following comminution and grindability testing. The gravity concentration proved more effective. Namely, magnetic separators could not process nor adequately separate beneficial non-ferrous elements because they were merged together with iron-bearing minerals and aluminosilicates in amorphous Pb-Zn slag grains. With the gravity concentration approach, 12.99% of the processed slag belonged to ∆T fraction (concentration of non-ferrous metal alloys), while remaining 87% corresponded to the tailings fraction (∆L). The total amounts of recovered Pb, Zn, Cu, and Ag from ∆T and ∆L fractions were 5.28%, 6.69%, 0.58%, and 76.12 ppm and 1.22%, 6.05%, 0.43%, and 15.26 ppm, respectively. This streamlined approach to valorizing Pb-Zn slag can reduce the need for hazardous chemicals used in hydrometallurgical refinement operations, as well as the extremely high temperatures required for pyrometallurgical processing. This is the first study to investigate the viability of this novel methodology, which involves the direct examinations of the Pb-Zn slag feed with various alternative technologies for separation and concentration. After extracting the valuable metals, the amorphous aluminosilicate part of the Pb-Zn slag can be reapplied as an alternative raw material in the building sector, adding to the circularity of the suggested approach.

Smelting used to be less efficient; therefore, wastes obtained from historical processing at smelter plants usually contain certain quantities of valuable metals. Upon the extraction of useful metal elements, metallurgical slag can be repurposed as an alternative mineral raw material in the building sector. A case study was conducted, which included an investigation of the physico-chemical, mineralogical, and microstructural properties of Pb–Zn slag found at the historic landfill near the Topilnica Veles smelter in North Macedonia. The slag was sampled using drill holes. The mineralogical and microstructural analysis revealed that Pb–Zn slag is a very complex and inhomogeneous alternative raw material with utilizable levels of metals, specifically Pb (2.3 wt.%), Zn (7.1 wt.%), and Ag (27.5 ppm). Crystalline mineral phases of wurtzite, sphalerite, galena, cerussite, akermanite, wüstite, monticellite, franklinite, and zincite were identified in the analyzed samples. The slag’s matrix consisted of alumino-silicates, amorphous silicates, and mixtures of spinel and silicates. Due to the economic potential of Pb, Zn, and Ag extraction, the first stage of reutilization will be to transform metal concentrates into their collective concentrate, from which the maximum amount of these crucial components can be extracted. This procedure will include combination of gravity concentration and separation techniques. The next step is to assess the Pb–Zn slag’s potential applications in civil engineering, based on its mineralogical and physico-mechanical properties. Alumino-silicates present in Pb–Zn slag, which contain high concentrations of SiO₂, Al₂O₃, CaO, and Fe₂O₃, are suitable for use in cementitious building composites. The goal of this research is to suggest a solution by which to close the circle of slag’s reutilization in terms of zero waste principles. It is therefore critical to thoroughly investigate the material, the established methods and preparation processes, and the ways of concentrating useful components into commercial products.

This paper presents the results of tests carried out to determine how the dosage of bentonite added as binder, affects the properties of green pellets made of the limestone fines that originate from Lithothamnium limestone processing. Bentonite was added to limestone in different mass fractions (1, 2.5, 5 and 10%), whereas all the other parameters of the pelletizing process remained constant. The aim of pelletizing was to consolidate limestone fines and form mechanically stable pellets, provided that all the other properties of limestone remain unchanged. The pellets formed in this way were analysed applying DTA/TG analysis and FTIR and SEM analyses. The results showed uniform distribution of bentonite in the pellets, demonstrated that the pellets are compact and there is no formation of new compounds. The pellets were tested for resistance to impact, compressive strength and abrasion resistance. Also disintegration tests were performed to determine the time required for the pellet to disintegrate completely in water. These mechanical properties are essential for transport, handling, storage and general use of pellets. The values of most of the parameters established for pellets with 5% bentonite, meet the standards required for use in agriculture for liming acid soils, however their application is limited because their impact resistance is unsatisfactory and the time required for their complete disintegration in water is extremely short. It should be noted that further increase of bentonite content (over 10%) will not improve the quality of green pellets. In view of the results obtained, it is necessary to introduce drying into the pelletizing process in order to bring the green pellets into solid state.

This review article surveys the subject of choice of high gradient magnetic separation processes for removal of Fe₂O₃ carriers from quartz raw material by electromagnetic separator with magnetic field intensity of 1.4 T.

The presented work offers a novel process scheme for valorizing historical Pb-Zn slag, which involves crushing, grinding, and then using separation techniques to concentrate valuable components (nonferrous metals). This methodology could have a significant impact on the global beneficiation of metallurgical slags since, in theory, it is significantly more simple, environmentally friendly, and cost-effective than standard pyrometallurgical or hydrometallurgical procedures. According to previous physicochemical and mineralogical studies, Pb-Zn slag from "Topilnica" Veles is a valuable secondary raw material. This inhomogeneous technogenic resource contains substantial amounts of nonferrous metals (Pb, Zn, Cu, and Ag). However, laboratory tests have indicated that the Pb-Zn slag contains a very uneven valuable metals amounts, ranging from several g/ton to several tens of g/ton. The main issue is that traditional metallurgical procedures for releasing beneficial elements are not commercially viable since the valuable elements are "trapped" within amorphous aluminosilicates or intergrowths of alloy grains and glassy phases. Gravity concentration (Wilfley 13 shaking table) and magnetic separation (Davis separator and disk separator) were used to obtain the final concentrate following comminution and grindability testing. The gravity concentration proved more effective. This streamlined approach of valorizing Pb-Zn slag can reduce the need for hazardous chemicals used in hydrometallurgical refinement operations, as well as the extremely high temperatures required for pyrometallurgical processing. This is the first investigation into the feasibility of this novel approach, which includes direct investigations of the Pb-Zn slag feed using these alternative technologies. After extracting the valuable metals, the amorphous aluminosilicate part of the Pb-Zn slag can be reapplied as an alternative raw material in the building sector, adding to the circularity of the suggested approach..

Aflatoxin B1 (AFB1) is one of the most toxic mycotoxins contaminating animal feed, and bentonite clays are widely used as adsorbents to reduce its bioavailability. This study introduces and characterizes a new, previously unexplored bentonite deposit from Bijelo Polje (Bar, Montenegro), with ~55% montmorillonite in the raw material. Size fractions (<0.200 mm, <0.037 mm, <0.005 mm) were obtained by sieving and centrifugation and characterized by laser diffraction, chemical composition, BET, CEC, and quantitative XRD (Rietveld). In vitro AFB1 adsorption (2–50 ppm, pH 3.0, 0.02% w/v adsorbent) simulated monogastric gastrointestinal conditions. Progressive size reduction increased smectite content (from ~55% to 91%), CEC (44–70 meq/100 g), purity, and BET specific surface area (26.5–50.8 m²/g), while reducing impurities and heavy metals to undetectable levels. The finest fraction (<0.005 mm) achieved the highest maximum adsorption capacity (q_max ≈ 240 mg/g), attributed to enhanced surface homogeneity and site accessibility, significantly outperforming coarser fractions and most unmodified natural bentonites. Only the 90% binding, low quartz/calcite). These results demonstrate that simple mechanical fractionation can yield exceptional performance in a novel natural raw material, offering a cost-effective, sustainable alternative to chemical modification for mycotoxin mitigation.