A mechanical property experiment was carried out on steel-polypropylene fiber-reinforced concrete after elevated temperatures by using a 50 mm diameter SHPB apparatus. The regulations of compressive strength, elastic modulus, Poisson’s ratio, and other mechanical properties under six heating temperature levels (normal temperature, 100 °C, 200 °C, 400 °C, 600 °C, and 800 °C) and three impact pressures (0.3 MPa, 0.4 MPa, 0.5 MPa) were studied. Using ANSYS/LS-DYNA 19.0 numerical simulation software and LS-PrePost post-processing software, numerical simulation analysis was conducted on the dynamic Hopkinson uniaxial impact compression and uniaxial dynamic impact splitting mechanical experiments of C40 plain concrete and steel-polypropylene hybrid fiber concrete. The results show that the dynamic compressive strength of hybrid fiber concrete with the optimal dosage reaches its maximum at a temperature group of 200 °C, and the dynamic compressive strength of hybrid fiber concrete with the optimal dosage increases by 97.1% compared to C40 plain concrete at a temperature group of 800 °C. The impact waveform and stress-strain curve results of the numerical simulation are very similar to the experimental results. The errors in calculating the peak stress and peak strain are within 6%, which can truly and accurately simulate the static mechanical properties and failure process of hybrid fiber-reinforced concrete.

The reciprocating shear mechanical properties and strength deterioration mechanisms of rockfill materials are of great research significance for high-fill slope stability analysis. To study the shear strength characteristics of argillaceous siltstone rockfill materials with different fabric characteristics under reciprocating shear loading, we analyzed the shear strength, hysteresis loop area, damping ratio, shear strength parameter, and shear stiffness of coarse-grained soils with different coarse grain contents using a coarse-grained soil direct shear testing machine capable of reciprocating shear and revealed their strength deterioration mechanism. The test results show that the shear strength of argillaceous siltstone rockfill materials is significantly affected by the coarse grain content and the number of reciprocating shears. Specifically, the shear strength increases with the coarse grain content and decreases with the number of reciprocating shears. The hysteresis loop area is positively correlated with the coarse grain content and negatively correlated with the number of reciprocating shears. The damping ratio is not related to the coarse grain content but tends to decrease with the number of reciprocating shears. Soil cohesion and the internal friction angle increase with the coarse grain content and decrease with the number of reciprocating shears. The soil failure shear stiffness is linearly correlated with the coarse grain content, and the normalized shear stiffness is logarithmically related to the number of reciprocating shears. According to these relationships, an empirical formula for the shear stiffness of argillaceous siltstone rockfill materials under different coarse grain contents and different numbers of reciprocating shears can be established to provide a basis for analyzing rockfill stability.