In the present work, magnesium oxide (MgO) and lead oxide (PbO) nanoparticles were prepared by the co-precipitation method. Their structural parameters and morphology were investigated using XRD, HRTEM, and FTIR. The formation of the phases was seen to have small average crystallite sizes and an orthorhombic crystal structure for both MgO and PbO nanoparticles. The results of HR-TEM showed irregularly shaped nanoparticles: quasi-spherical or rod-like shapes and spherical-like shapes for MgO and PbO nanoparticles, respectively. The produced nanoparticles’ size using X-ray diffraction analysis was found to be 17 nm and 41 nm for MgO and PbO nanoparticles, respectively. On the other hand, it was observed from the calculations that the optical band gap obeys an indirect allowed transition. The calculated values of the band gap were 4.52 and 4.28 eV for MgO and PbO NPs, respectively. The MB was extracted from the wastewater using the prepared composites via absorption. Using a variety of kinetic models, the adsorptions were examined. Out of all the particles, it was discovered that the composites were best. Furthermore, of the models currently under consideration, the pseudo-second-order model best fit the degradation mechanism. The resultant composites could be beneficial for degrading specific organic dyes for water purification, as well as applications needing a wider optical band gap.

Zinc sulfide (ZnS) nanoparticles were fabricated using the chemical precipitation method. The X-ray diffraction (XRD), Raman spectroscopy, and scanning electron microscopy (SEM) techniques were used to investigate the structural parameters of the formed ZnS. The hexagonal crystal structure of the Zn and ZnS phases was formed. The average crystallite size of the ZnS phase is 10.3 nm, which is much smaller than that of the Zn phase (54.5 nm). Several frequencies and phonon modes were detected in the Raman scattering spectrum belonging to the ZnS nanoparticles. The synthesized ZnS nanoparticles were used as catalysts to eliminate the Congo red (CR) dye, with different concentrations, from synthetic wastewater. The impact of the CR dye concentration and shaking period on the adsorption of CR was thoroughly investigated, and various adsorption kinetic models were tested. After 3 h of shaking, the adsorption efficiency reached 26.01% for 40 mg/L CR dye and 27.84% for 20 mg/L CR dye. The adsorption capacities of the CR dye in the presence of ZnS are 16% and 9% for 40 and 20 mg/L, respectively. Based on the correlation factor, the intraparticle diffusion kinetic model was considered the best of the tested models.

This work comprehensively studies both the photocatalytic degradation and the adsorption process of Congo red dye on the surface of a mixed-phase copper oxide–graphene heterostructure nanocomposite. Laser-induced pristine graphene and graphene doped with different CuO concentrations were used to study these effects. Raman spectra showed a shift in the D and G bands of the graphene due to incorporating copper phases into the laser-induced graphene. The XRD confirmed that the laser beam was able to reduce the CuO phase to Cu₂O and Cu phases, which were embedded into the graphene. The results elucidate incorporating Cu₂O molecules and atoms into the graphene lattice. The production of disordered graphene and the mixed phases of oxides and graphene were validated by the Raman spectra. It is noted from the spectra that the D site changed significantly after the addition of doping, which indicates the incorporation of Cu₂O in the graphene. The impact of the graphene content was examined with 0.5, 1.0, and 2.0 mL of CuO. The findings of the photocatalysis and adsorption studies showed an improvement in the heterojunction of copper oxide and graphene, but a significant improvement was noticed with the addition of graphene with CuO. The outcomes demonstrated the compound’s potential for photocatalytic use in the degradation of Congo red.

International audienceThis paper highlights some interesting results regarding the Single walled carbon nanotubes (SWCNTs) functionalized by carboxylic acid, which were dispersed with ultrasonic vibration and implanted using 3 aminopropyltriethoxysilane (APTES) solution on a porous pyramidal silicon (PPS) surface. The physical characterizations of the samples were studied by both Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Also, Fourier transform infrared spectroscopy (FTIR) has been carried out. First, SEM morphological observations reveals that nano pores dig into the sides of the micro pyramids and SWCNTs located throughout the area Si pyramidal structure. Second, AFM confirm the information ob tained by various other techniques such those of electron microscopy. Third, Fourier transform infrared spectroscopy (FTIR) analysis confirms the chemical bonding between the silicon and SWCNTs. Finally, a graphical abstract is proposed to describe the implantation steps of SWCNTs on the porous silicon (pSi) having pyramidal structure