The effect of laser cladding on the surface microstructure and corrosion properties of coated/uncoated specimens were investigated. Fe-based alloy coating was produced on 35CrMo steel by laser cladding. The phase composition, microstructure, interface element distribution, microhardness and corrosion resistance of the cladding coating were measured. The results show that the cladding layer is mainly composed of α-Fe phases, the microstructure presents a gradient distribution, and a good metallurgical bond is formed at the boundary with the substrate. Microhardness profiles show that the average microhardness of the cladding coating is about 2.1 times higher than that of the uncoated specimen. In addition, the electrochemical results show that the coated specimen exhibits far better corrosion resistance than to the uncoated specimen.

Ultrasonic treatment was applied during solidification forming of 6016 aluminium alloys. The effects of ultrasonic vibration on the microstructure and mechanical properties of the 6016 aluminium alloy ingot were studied. Compared with conventional casting, the ingot prepared with ultrasound applied to the molten metal had a fully refined microstructure and greater material homogeneity. Ultrasonic treatment reduced the amount of porosity developed by embedded gas and also resulted in an obvious decrease in solidification defects, like shrinkage. In addition, component segregation was minimised and the mechanical properties were enhanced.

The effects of ultrasonic treatment (UST) on the solidification microstructure of a 35CrMo steel cast ingot were investigated. To avoid the erosion of a high-temperature melt, a T-shaped ultrasonic waveguide unit was used to introduce ultrasonic vibrations into a 35CrMo steel die casting melt. The experimental results show that the microstructure of the ingot was refined by ultrasonic treatment. While the microstructure of untreated 35CrMo steel is coarse dendritic grains, after the introduction of ultrasonic treatment, the solidification microstructure transforms from coarse dendritic to equiaxed grains, and the dendrites are also refined. Samples from different positions of the ingots were subjected to different ultrasonic effects, and the effects on grain refinement also varied due to the severe attenuation of the ultrasound in the melt. The mechanisms of grain refinement using ultrasonic treatment for 35CrMo steel melt are presented.

In order to achieve long-term and stable ultrasonic treatment in the direct chill semi-continuous casting process, a new L-shaped ceramic ultrasonic wave guide rod is designed to introduce ultrasonic bending vibration into 2A14 aluminum alloy melt. The effect of ultrasonic bending vibration on the solidification structure and composition segregation of large 2A14 aluminum alloy ingots (φ 830 mm × 6000 mm) in the process of semi-continuous casting were studied by means of a direct reading spectrometer, scanning electron microscope, metallographic microscope, and hardness test. The ultrasonic ingot treated by bending vibration was compared with the ingot without ultrasonic treatment and the ingot treated by the traditional straight-rod titanium alloy wave guide rod. The results show that, during the solidification of 2A14 aluminum alloy, ultrasonic treatment can significantly refine the grain, break up the agglomerated secondary phase, and make its distribution uniform. The macro-segregation degree of solute including the negative segregation at the edge of the ingots and the positive segregation in the center can be reduced. Through comparative analysis, the macrostructure of the ingot, treated by the L-shaped ceramic ultrasonic wave guide rod, was found to be better than that of the ingot treated by the traditional straight-rod titanium alloy wave guide rod. In particular, the grain refinement effect at the edge of the ingot was the best, the secondary phase was smaller, more solute elements can be dissolved into the α-Al matrix, and the ability of the L-shaped ultrasonic wave guide rod to restrain segregation was stronger at the edge of the ingot.

The effects of ultrasonic-aided quenching (USQ) on the microstructure and corrosion properties of 35CrMoV steel in a simulated seawater environment (wt % (NaCl) = 3.5) were studied. The corrosion properties of the steel were studied by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves. The scanning electron microscope (SEM) and energy dispersive spectrometer (EDS) were used to characterize the microstructure and corrosion products. Combined with the EIS equivalent circuit, the corrosion mechanism was investigated. The results show that the microstructure of the USQ specimen is small martensite and that there was no residual ferrite compared with an un-ultrasonic-aided quenching (UUSQ) sample. It was also found that the corrosion products of USQ sample are less than the UUSQ sample, and the corrosion cracks are lighter and thinner than that of the UUSQ sample, which indicates that the corrosion resistance of 35CrMoV in a seawater environment has been obviously improved.

In order to achieve the industrial application of ultrasonic energy in the continuous casting and rolling production of aluminum alloy, a new type of L-shaped ultrasonic rod was used to introduce an ultrasonic bending vibration into the aluminum melt in the launder during the horizontal twin-roll continuous casting and rolling process of a 1060 aluminum alloy. The effects of the ultrasonic bending vibration on the microstructure and properties of the 1060 aluminum alloy cast rolling strip and its subsequent cold rolling strip were studied experimentally, and the effect of the ultrasonic-assisted refining with different amounts of Al-Ti-B refiner was explored. The results show that under the same addition amount of Al-Ti-B refiner, the ultrasonic bending vibration can refine the grains of the cast rolling strip, make the distribution of precipitates more uniform, reduce the slag inclusion defects, and improve the mechanical properties to a certain extent. The microstructure and properties of the ultrasonic cast rolling strip with 0.18 wt% Al-Ti-B refiner or 0.12 wt% Al-Ti-B refiner are better than those of the conventional cast rolling strip, but the microstructure and properties of the ultrasonic cast rolling strip with 0.09 wt% Al-Ti-B refiner are slightly worse than those of the conventional cast rolling strip. Moreover, after cold rolling, the effect of the ultrasonic bending vibration on the improvement of the microstructure and properties of the aluminum alloy strip is inherited. A comprehensive analysis shows that the use of ultrasonic energy in this paper cannot completely replace the effect of the Al-Ti-B refiner, but it can reduce the addition amount of the Al-Ti-B refiner by 1/3.