In order to achieve long-term and stable ultrasonic treatment in the direct chill semi-continuous casting process, a new L-shaped ceramic ultrasonic wave guide rod is designed to introduce ultrasonic bending vibration into 2A14 aluminum alloy melt. The effect of ultrasonic bending vibration on the solidification structure and composition segregation of large 2A14 aluminum alloy ingots (φ 830 mm × 6000 mm) in the process of semi-continuous casting were studied by means of a direct reading spectrometer, scanning electron microscope, metallographic microscope, and hardness test. The ultrasonic ingot treated by bending vibration was compared with the ingot without ultrasonic treatment and the ingot treated by the traditional straight-rod titanium alloy wave guide rod. The results show that, during the solidification of 2A14 aluminum alloy, ultrasonic treatment can significantly refine the grain, break up the agglomerated secondary phase, and make its distribution uniform. The macro-segregation degree of solute including the negative segregation at the edge of the ingots and the positive segregation in the center can be reduced. Through comparative analysis, the macrostructure of the ingot, treated by the L-shaped ceramic ultrasonic wave guide rod, was found to be better than that of the ingot treated by the traditional straight-rod titanium alloy wave guide rod. In particular, the grain refinement effect at the edge of the ingot was the best, the secondary phase was smaller, more solute elements can be dissolved into the α-Al matrix, and the ability of the L-shaped ultrasonic wave guide rod to restrain segregation was stronger at the edge of the ingot.

In order to improve the performances of large-size 35CrMoV cast ingot, ultrasonic flexural vibration was guided into 35CrMoV steel melt through L-shaped ultrasonic waveguide rod during the solidification, and the effects of ultrasonic flexural vibration on macrostructure, microstructure, and mechanical properties of large-size 35CrMoV cast ingot were investigated. It is found that the columnar crystal zone has disappeared and the ingot is composed of the equiaxed crystals present in the ultrasonic ingot. The size of grains treated by ultrasonic are significantly smaller than conventional ingot. The distribution of ferrite in matrix structure is also more uniform than conventional ingot. The tensile strength is increased by 3.14%∼17.12%, and the elongation is increased by 39.13%∼287.50% compared with the conventional ingot at different positions.