The features of uranium mining on Kazakhstan’s enterprises have been examined, and uranium deposits located in the Syrdarya and Shu-Sarysu depressions have been described. Actual and projected data on the development of technological blocks in areas with complex geological structures have been analyzed and compared. Core samples were collected and, using X-ray diffraction analysis, quantitative and qualitative characteristics as well as mineral compositions of ores from various productive horizons of uranium deposits in the Syrdarya and Shu-Sarysu depressions were comparatively analyzed. It was determined that the ores in the Syrdarya depression are relatively homogeneous compared to those in the Shu-Sarysu depression, although in some places, clay minerals and gypsum are present, which hinder the uranium leaching processes. In the ores of the Shu-Sarysu depression, clay minerals that impede the uranium leaching processes are present in certain areas. Microscopic analysis of core material samples using a LEICA DM 2500 P microscope revealed particle sizes and shapes, as well as their distribution within the structure of host rocks in the productive horizon. Using X-ray diffraction analysis, mineral compositions of sediment-forming components during uranium well mining in the considered productive horizons were determined and comparatively analyzed. It was established that in the geotechnological wells of the Syrdarya depression, sediments of predominantly chemical origin, such as gypsum, are formed. However, in the geotechnological wells of the Shu-Sarysu depression, sediments of mechanical origin, consisting predominantly of quartz particles and clay minerals, are formed. Based on the obtained data, a method for intensifying underground uranium leaching in complex geological conditions has been developed, which involves dissolving sediment formations and increasing the oxidative–reductive potential of the leaching solution. The proposed and experimentally substantiated universal methodology for enhancing uranium well production involves the dissolution and prevention of precipitation using hydrofluoric acid solutions, as well as the oxidation of uranium dioxide with hydrogen peroxide.

The article presents the results of the study and analysis of the mining and geological features of the object of study, which made it possible to identify the main reason for the decrease in the flow rate of pumping wells due to the colmatation of filters and the filter part of wells due to the predominance of silicon compounds in the array. Therefore, the technology of decolmatization of filters and the filter part of wells is proposed and the results of pilot work to increase the flow rate of pumping wells during underground borehole leaching of uranium using ammonium bifluoride are presented. Comparative results before and after treatment of the leaching solution with ammonium bifluoride showed that the flow rate of various pumping wells increased from 1.4 to 4.4 m3/h, and in others – from 2 to 5.3 m3/h Мақалада зерттеу объектісінің тау-кен геологиялық ерекшеліктерін зерттеу және талдау нәтижелері келтірілген, бұл массивте кремний қосылысының басым болуына байланысты сүзгілер мен ұңғымалардың сүзгі бөлігінің колматациясына байланысты сорғы ұңғымаларының дебитінің төмендеуінің негізгі себебін анықтауға мүмкіндік берді. Сондықтан сүзгілерді және ұңғымалардың сүзгі бөлігін декольматациялау технологиясы ұсынылды және аммоний бифторидін қолдана отырып, уранды жерасты ұңғымасымен шаймалау кезінде сорғы ұңғымаларының дебитін арттыру бойынша тәжірибелік-өнеркәсіптік жұмыстардың нәтижелері келтірілген. Бифторидті аммониймен шаймалау ерітіндісін өңдеуге дейінгі және кейінгі салыстырмалы нәтижелер әртүрлі сорғы ұңғымаларының дебиті сағатына 1,4-тен 4,4 м3 дейін, ал басқаларында сағатына 2-ден 5,3 м3 дейін өскенін көрсетті В статье приведены результаты изучения и анализа горно-геологических особенностей объекта исследования, что позволило выявить основную причину снижения дебита откачных скважин из-за кольматации фильтров и прифильтровой части скважин за счет преобладания в массиве соединении кремния. Поэтому предложена технология декольматации фильтров и прифильтровой части скважин и приведены результаты опытно-промышленных работ по повышению дебита откачных скважин при подземном скважинном выщелачивании урана с применением бифторида аммония. Сравнительные результаты до и после обработки выщелачивающим раствором бифторид аммонием показали, что дебит различных откачных скважин увеличились с 1,4 до 4,4 м3/ч, а в других – с 2 до 5,3 м3/ч