Recently, deep cryogenic treatment is performed to improve the mechanical responses (wear, hardness, fatigue, and thermal conductivity) of various steel components. Researchers have tried to evaluate the eco-friendly and nontoxic process to optimize the parameters. Cold-shearing punches used to manufacture various holes that undergo severe impact loading and wear in the metal forming process. This study concerns the effect of soaking time (24 hr, 36 hr) at liquid nitrogen temperature (−145 °C) during the deep cryogenic treatment on the microstructural changes which are carbide distribution and retained austenite percentage of AISI D3 tool steel punches. It was shown that the deep cryogenic treatment reduces retained austenite and enhanced uniform distribution of carbide particles. It is concluded that for significantly improved punch life and performance, it is an advisable application of 36 hr deep cryogenic treatment.

The inhibition effect of mimosa extract on the corrosion of AA6060 aluminum alloy in acid rain solution was investigated by electrochemical impedance spectroscopy and dynamic electrochemical impedance spectroscopy (DEIS). All the studied electrochemical parameters showed good corrosion inhibitive characteristics with respect to the aluminum alloy in the tested solution. Inhibitor efficiency increased with the concentration and attained 45% at 2750 ppm. The advantage of DEIS as a tool for the investigation of corrosion inhibitor influence was discussed.