High-entropy alloys (HEAs) are recognized as a class of advanced materials with outstanding mechanical properties and corrosion resistance. Among these, nickel-based HEAs stand out for their impressive strength, ductility, and oxidation resistance. This review delves into the latest advancements in nickel-containing HEAs, covering their fundamental principles, alloy design strategies, and additive manufacturing techniques. We start by introducing HEAs and their unique properties, emphasizing the crucial role of nickel. This review examines the complex relationships between alloy composition, valence electron concentration (VEC), and the resulting crystal structures. This provides insights into design principles for achieving desired microstructures and mechanical properties. Additive manufacturing (AM) techniques like selective laser melting (SLM), electron beam melting (EBM), and laser metal deposition (LMD) are highlighted as powerful methods for fabricating intricate HEA components. The review addresses the challenges of AM processes, such as porosity, fusion defects, and anisotropic mechanical properties, and discusses strategies to mitigate these issues through process optimization and improved powder quality. The mechanical behavior of AM-processed nickel-based HEAs is thoroughly analyzed, focusing on compressive strength, hardness, and ductility. This review underscores the importance of microstructural features, including grain size, phase composition, and deformation mechanisms, in determining the mechanical performance of these alloys. Additionally, the influence of post-processing techniques, such as heat treatment and hot isostatic pressing (HIP) on enhancing mechanical properties is explored. This review also examines the oxidation behavior of nickel-containing HEAs, particularly the formation of protective oxide scales and their dependence on aluminum content. The interplay between composition, VEC, and oxidation resistance is discussed, offering valuable insights for designing corrosion resistant HEAs. Finally, this review outlines the potential applications of nickel-based HEAs in industries such as aerospace, automotive, and energy, and identifies future research directions to address challenges and fully realize the potential of these advanced materials.

While binder jetting (BJ) additive manufacturing (AM) holds considerable promise for industrial applications, defects often compromise part quality. This study addresses these challenges by investigating binding mechanisms and analyzing common defects, proposing tailored solutions to mitigate them. Emphasizing defect identification for effective quality control in BJ-AM, this research offers strategies for in-process rectification and post-process evaluation to elevate part quality. It shows how to successfully process metallic parts with complex geometries while maintaining consistent material properties. Furthermore, the paper explores the microstructure of AISI M2 tool steel, utilizing advanced image processing techniques like digital image analysis and SEM images to evaluate carbide distribution. The results show that M2 tool steel has a high proportion of M₆C carbides, with furnace-cooled samples ranging from ~2.4% to 7.1% and MC carbides from ~0.4% to 9.4%. M₆C carbides ranged from ~2.6% to 3.8% in air-cooled samples, while water-cooled samples peaked at ~8.52%. Sintering conditions also affected shrinkage, with furnace-cooled samples showing the lowest rates (1.7 ± 0.4% to 5 ± 0.4%) and water-cooled samples showing the highest (2 ± 0.4% to 14.1 ± 0.4%). The study recommends real-time defect detection systems with autonomous corrective capabilities to improve the quality and performance of BJ-AM components.

The versatility of titanium (Ti) allows it to be employed in various industries, from aerospace engineering to medical technology, highlighting its significance in modern manufacturing and engineering processes. Spark plasma sintering (SPS) is currently being explored to enhance its properties further and broaden its application range. The current study focuses on exploring and optimizing the effect of SPS temperature (800, 900, 1000, 1100, 1200, and 1400 °C) on pure Ti sintered at 60 MPa in a controlled argon environment with a dwell time of 5 min. All the prepared samples were highly dense with a relative density above 99%, but exhibited significant variations in grain size (10 to 57 µm), tensile yield strength (488 to 700 MPa), ultimate tensile strength (597 to 792 MPa), and ductility (4 to 7%). A microstructural investigation was performed using XRD, SEM, and EDS to predict the influence of sintering temperature on the formation of different phases. The XRD patterns of all sintered samples showed the presence of single-phase α-Ti with hexagonally close-packed Ti. This work is a step forward in optimizing SPS-processed Ti’s physical and mechanical properties for enhanced structural and biomedical applications.

Titanium (Ti) is widely used in structural, maritime, aerospace, and biomedical applications because of its outstanding strength-to-weight ratio, superior corrosion resistance, and excellent biocompatibility. However, the lower surface hardness and inferior wear resistance of the Ti and Ti alloys limit their industrial applications. Coating Ti surfaces can initiate new possibilities to give unique characteristics with significant improvement in the Ti component’s functionality. The current research designed and synthesized titanium nitride (TiN), titanium carbide (TiC), titanium carbonitride (TiCN), tantalum nitride (TaN), and niobium nitride (NbN) ceramic coating layers (400 µm) over a Ti substrate using a spark plasma sintering process (SPS). The coatings on the Ti substrate were compact and consolidated at an SPS temperature of 1500 °C, pressure of 50 MPa, and 5 min of holding time in a controlled argon atmosphere. Microstructure investigation revealed a defect-less coating-substrate interface formation with a transition/diffusion zone ranging from 10 µm to 20 µm. Among all of the ceramic coatings, titanium carbide showed the highest improvement in surface hardness, equal to 1817 ± 25 HV, and the lowest coefficient of friction, equal to 0.28 for NbN.

Nowadays Energy is becoming a crucial part of human needs and it’s essential for the day to day activities. We use an enormous amount of energy either from fossil fuels, electricity, or solar to heat the water to fulfil the need of residential or industrial sectors, and unfortunately, we consciously lose out a significant amount of energy in the form of heat from the condensers of air conditioning. Hence conservation of energy and its effective utilization has become imperative. The main objective of this research paper is to demonstrate how the waste heat which is dissipated from the condenser coil of a 1-ton Air conditioner is being utilized for heating the water and used to increase the Coefficient of Performance (COP) of the system. Therefore, by redesigning the condenser part of AC we would be able to appease the necessity of the heated water for bathing, cleaning, space heating, etc. in hostels, restaurants, for domestic and industrial use as a primary unit or with a hybrid water heater system.