An enhancement of the local electric field at the metal/dielectric interface of hybrid materials due to the localized surface plasmon resonance (LSPR) phenomenon plays a particularly important role in versatile research fields resulting in a distinct modification of the electrical, as well as optical, properties of the hybrid material. In this paper, we succeeded in visually confirming the LSPR phenomenon in the crystalline tris(8-hydroxyquinoline) aluminum (Alq₃) micro-rod (MR) hybridized with silver (Ag) nanowire (NW) in the form of photoluminescence (PL) characteristics. Crystalline Alq₃ MRs were prepared by a self-assembly method under the mixed solution of protic and aprotic polar solvents, which could be easily applied to fabricate hybrid Alq₃/Ag structures. The hybridization between the crystalline Alq₃ MRs and Ag NWs was confirmed by the component analysis of the selected area electronic diffraction attached to high-resolution transmission electron microscope. Nanoscale and solid state PL experiments on the hybrid Alq₃/Ag structures using a lab-made laser confocal microscope exhibited a distinct enhancement of the PL intensity (approximately 26-fold), which also supported the LSPR effects between crystalline Alq₃ MRs and Ag NWs.

We experimentally demonstrate the direct visualization of ultraviolet (UV) light using flexible polymer composite films consisting of crystalline organic tris-(8-hydroxyquinoline) aluminum (Alq3) micro-rods and polydimethylsiloxane (PDMS). The representative organic mono-molecule Alq3, which is a core material of organic light-emitting diodes, was used to detect light in the invisible UV region and visualize photoluminescence (PL). Alq3 shows absorption in the UV region and light-emitting characteristics in the green region, making it an optimal material for UV visualization because of its large Stokes transition. Crystalline Alq3 micro-rods were fabricated in a deionized water solution through a sequential process of reprecipitation and self-assembly. Highly bright photoluminescence was observed on the highly crystalline Alq3 micro-rods under UV light excitation, indicating that the crystalline structures of Alq3 molecules affect the visible emission decay of excitons. The Alq3 micro-rods were manufactured as flexible polymer composite films using a PDMS solution to observe UV photodetector characteristics according to UV intensity, and it was confirmed that the intensity of the fine UV light reaching the earth’s surface can be visualized by making use of this UV photodetector.