Microplastics (MPs) have attracted considerable attention as one of the most remarkable food and drink pollutants in recent years. Disposable cups, which are widely used as single-use containers, have been suspected as the primary sources of MPs found in cold and hot beverages. In this study, the effect of different exposure times (0, 5, 10 and 20 min) and temperatures (4 °C, 50 °C and 80 °C) on MP release from the single-use cups made of four different materials [polypropylene (PP), polystyrene (PS), polyethylene (PE) coated paper cups and expanded polystyrene (EPS)] into the water was investigated. The number of MPs ranged from 126 p/L to 1420 p/L, while the highest and lowest counts were observed in the PP (50 °C for 20 min) and PE-coated paper cups (4 °C 0 min), respectively. Washing the cups with ultrapure water prior to use reduced the MP release by 52–65%. SEM images demonstrated the abrasion on the surface of the disposable cups as a result of hot water exposure. Intensities of FTIR absorbance levels at some wavelengths were decreased by the water treatment, which could be evidence of surface abrasion. The annual MP exposure of consumers was calculated as 18,720–73,840 by the consumption of hot and cold beverages in disposable cups. In conclusion, as the level and potential toxicity of MP exposure in humans are not yet fully known, this study sheds light on the number of MPs transferred to cold and hot beverages from single-use disposable cups.

To valorize abundant, unexploited, and low‐cost agro‐industrial by‐products, olive pomace is proposed as a sustainable and renewable raw material for cellulose microfibers (CMFs) production. In this study, CMFs were extracted from olive pomace using alkaline and bleaching treatments and characterized in terms of morphological, structural, and thermal properties. Afterward, the reinforcing capability of microfibers was examined using carboxymethyl cellulose (CMC) as a polymer matrix by the solvent casting process. The effects of CMF loading (1%, 3%, 5%, and 10%) on the composites' mechanical, physical, morphological, and thermal properties were assessed. CMF incorporation led to a decrease in moisture content (MC), water solubility (WS), and water vapor permeability (WVP) and an increase in tensile strength (TS), stiffness and transparency values, and thermal stability of CMC films. Increasing CMF content to 5%, increased the TS and elasticity modulus by 54% and 79%, respectively, and reduced the WVP and light transmissivity at 280 nm, by 22% and 47%, respectively. The highest water, moisture, light barrier, and mechanical properties of composites were reached at 5% CMFs.