Directing efficient hole transport: Surface defects in three-dimensional perovskites can decrease performance but can be healed with coatings based on two-dimensional (2D) perovskite such as Ruddlesden-Popper phases. However, the bulky organic groups of these 2D phases can lead to low and anisotropic charge transport. F. Zhang et al . show that a metastable polymorph of a Dion-Jacobson 2D structure based on asymmetric organic molecules reduced the energy barrier for hole transport and their transport through the layer. When used as a top layer for a triple-cation mixed-halide perovskite, a solar cell retained 90% of its initial power conversion efficiency of 24.7% after 1000 hours of operation at approximately 40°C in nitrogen. —PDS

Metal halide perovskite semiconductors possess outstanding characteristics for optoelectronic applications including but not limited to photovoltaics. Low-dimensional and nanostructured motifs impart added functionality which can be exploited further. Moreover, wider cation composition tunability and tunable surface ligand properties of colloidal quantum dot (QD) perovskites now enable unprecedented device architectures which differ from thin-film perovskites fabricated from solvated molecular precursors. Here, using layer-by-layer deposition of perovskite QDs, we demonstrate solar cells with abrupt compositional changes throughout the perovskite film. We utilize this ability to abruptly control composition to create an internal heterojunction that facilitates charge separation at the internal interface leading to improved photocarrier harvesting. We show how the photovoltaic performance depends upon the heterojunction position, as well as the composition of each component, and we describe an architecture that greatly improves the performance of perovskite QD photovoltaics.

Achieving long-term operational stability at a high efficiency level for perovskite solar cells is the most challenging issue toward commercialization of this emerging photovoltaic technology. Here, we investigated the cooperation of a Lewis base and a Lewis acid by combining commercial bis-PCBM mixed isomers as the Lewis acid in the antisolvent and N-(4-bromophenyl)thiourea (BrPh-ThR) as the Lewis base in the perovskite solution precursor. The combination of the Lewis base and the Lewis acid synergistically passivates Pb²⁺ and PbX³⁻ antisite defects, enlarges the perovskite grain size, and improves charge-carrier separation and transport, leading to improved device efficiency from 19.3% to 21.7%. In addition, this Lewis base and acid combination also suppresses moisture incursion and passivates pinholes generated in the hole-transporting layer. The unsealed devices remained at 93% of the initial efficiency value in ambient air (10–20% relative humidity) after 3600 h at 20–25 °C and dropped by 10% after 1500 h under continuous operation at 1-sun illumination and 55 °C in nitrogen with maximum power-point tracking.