In our study, transparent and conductive films of NiO_x were successfully deposited by sol-gel technology. NiO_x films were obtained by spin coating on glass and Si substrates. The vibrational, optical, and electrical properties were studied as a function of the annealing temperatures from 200 to 500 °C. X-ray Photoelectron (XPS) spectroscopy revealed that NiO was formed at the annealing temperature of 400 °C and showed the presence of Ni⁺ states. The optical transparency of the films reached 90% in the visible range for 200 °C treated samples, and it was reduced to 76–78% after high-temperature annealing at 500 °C. The optical band gap of NiOx films was decreased with thermal treatments and the values were in the range of 3.92–3.68 eV. NiO_x thin films have good p-type electrical conductivity with a specific resistivity of about 4.8 × 10⁻³ Ω·cm. This makes these layers suitable for use as wideband semiconductors and as a hole transport layer (HTL) in transparent solar cells.

The present work explores in detail the effect of alkaline-basic electrolytes on the capacitance performance of biomass-derived carbonaceous materials used as electrodes in symmetric supercapacitors. The proof-of-concept is demonstrated by two commercial carbon products (YP-50F and YP-80F, Kuraray Europe GmbH, Vantaa, Finland), obtained from coconuts. The capacitance performance of YP-50F and YP-80F was evaluated in three types of basic electrolytes: 6 M LiOH, 6 M NaOH and 6 M KOH. It was found that the capacitance performance of YP-50F improved in the following order: NaOH < LiOH < KOH; Meanwhile, for YP-80F, the order changes to LiOH < NaOH < KOH. After 1000 cycles, the cycling stability of both YP-50F and YP-80F increased in the order NaOH < LiOH < KOH. This order of performance improvement is determined by both the electrolyte conductivity and the interaction between the functional groups of carbonaceous materials and alkaline electrolytes. The reactivity of the functional groups was assessed by postmortem SEM/EDS and X-ray photoelectron spectroscopy (XPS) analyses of the electrodes after prolonged cycling.