This study aims to produce polypropylene (PP)/titanium dioxide (TiO₂) melt-blown membranes for oil/water separation and photocatalysis. PP and different contents of TiO₂ are melt-blended to prepare master batches using a single screw extruder. The master batches are then fabricated into PP/TiO₂ melt-blown membranes. The thermal properties of the master batches are analyzed using differential scanning calorimetry and thermogravimetric analysis, and their particle dispersion and melt-blown membrane morphology are evaluated by scanning electron microscopy. TiO₂ loaded on melt-blown membranes is confirmed by X-ray diffraction (XRD). The oil/water separation ability of the melt-blown membranes is evaluated to examine the influence of TiO₂ content. Results show that the thermal stability and photocatalytic effect of the membranes increase with TiO₂ content. TiO₂ shows a good dispersion in the PP membranes. After 3 wt.% TiO₂ addition, crystallinity increases by 6.4%, thermal decomposition temperature increases by 25 °C compared with pure PP membranes. The resultant PP/TiO₂ melt-blown membrane has a good morphology, and better hydrophobicity even in acetone solution or 6 h ultraviolet irradiation, and a high oil flux of about 15,000 L·m⁻²·h⁻¹. Moreover, the membranes have stabilized oil/water separation efficiency after being repeatedly used. The proposed melt-blown membranes are suitable for mass production for separating oil from water in massively industrial dyeing wastewater.

Particulate matter 2.5 (PM_2.5) has become a public hazard to people’s lives and health. Traditional melt-blown membranes cannot filter dangerous particles due to their limited diameter, and ultra-fine electrospinning fibers are vulnerable to external forces. Therefore, creating highly efficient air filters by using an innovative technique and structure has become necessary. In this study, a combination of polypropylene (PP) melt-blown and polyvinyl alcohol (PVA)/zeolite imidazole frameworks-8 (ZIF-8) electrospinning technique is employed to construct a PP/PVA/ZIF-8 membrane with a hierarchical fibrous structure. The synergistic effect of hierarchical fibrous structure and ZIF-8 effectively captures PM_2.5. The PP/PVA composite membrane loaded with 2.5% loading ZIF-8 has an average filtration efficacy reaching as high as 96.5% for PM_2.5 and quality factor (Q_f) of 0.099 Pa⁻¹. The resultant membrane resists 33.34 N tensile strength and has a low pressure drop, excellent filtration efficiency, and mechanical strength. This work presents a facile preparation method that is suitable for mass production and the application of membranes to be used as air filters for highly efficient filtration of PM_2.5.

In this article, expanded vermiculite (EV)-enhanced polyurethane foam bionic composites inspired by pomelo peel is proposed. The columnar lattice structure mold is employed to constitute the periodic interface structure and gradient foam structure, and the nylon nonwoven fabric is combined as the surface layer. The effects of EV content on the thermal, compression, and dynamic cushion properties of bionic composites are investigated. Results show that residual char increases with EV content, which conduces to decrease the release of heat flow. The proposed bionic composite with columnar lattice structure has optimal compressive modulus, energy absorption and dynamic cushion efficacy when 1 wt% EV is added. However, its performance decreases slowly when EV fillers are continuously added because the cell morphology is changed from round to irregular shape and the interfacial adhesion of filler–matrix is weakened. Owing to their unique bionic structure, composites can absorb 99% of the energy impacted by flat impactor within a smaller deformation and achieve 97% absorption efficiency for a hemispheric impactor in cushion test.

The orifice coagulation bath method is proposed to encapsulate shear thickening fluid (STF) to form STF capsules, in an attempt to improve the combination of STF and the matrix as well as strengthen the flexibility and stability of the STF composites. By varying the calcium chloride concentration (10, 20 mg/mL), sodium alginate concentration (5, 7, 10 mg/mL) and the surfactant dosage (10%, 20%, 30%), optimal preparation conditions were studied, considering the capsule strength and encapsulation rate. The capsules were also characterized using a scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FTIR) and a thermogravimetric analyzer (TGA). The results show that the optimal solution for the preparation of the capsules is composed of 30% surfactant, 10 mg/mL mass concentration of CaCl₂, and 10 mg/mL mass concentration of sodium alginate. The rough surface and porous interior was observed by SEM. The average diameter of the capsules was 1.93 mm. The TGA curves indicate an improvement on the capsule thermal stability. This study thus provides a promising STF capsule preparation method.

With the aim of achieving controllable mass production of electrospun nanofiber films, this study proposes and investigates the feasibility of using a custom-made linear electrode- electrospun device to produce conductive graphene (GR)-filled polyvinyl alcohol (PVA) nanofibers. The film morphology and diameter of nanofibers are observed and measured to examine the effects of viscosity and conductivity of the PVA/GR mixtures. Likewise, the influence of the content of graphene on the hydrophilicity, electrical conductivity, electromagnetic interference shielding effectiveness (EMSE), and thermal stability of the PVA/GR nanofiber films is investigated. The test results show that the PVA/GR mixture has greater viscosity and electric conductivity than pure PVA solution and can be electrospun into PVA/GR nanofiber films that have good morphology and diameter distribution. The diameter of the nanofibers is 100 nm and the yield is 2.24 g/h, suggesting that the process qualifies for use in large-scale production. Increasing the content of graphene yields finer nanofibers, a smaller surface contact angle, and higher hydrophilicity of the nanofiber films. The presence of graphene is proven to improve the thermal stability and strengthens the EMSE by 20 dB at 150–1500 MHz. Mass production is proven to be feasible by the test results showing that PVA/GR nanofiber films can be used in the medical hygiene field.