The aim of this study was to develop a polyethylene/polyamide (R-PE/R-PA) regranulated product made from post-consumer wastes grafted with polyethylene-graft-maleic anhydride (PE-g-MAH) by reactive extrusion in a twin-screw extruder equipped with an external mixing zone. The compatibility effect of PE-g-MAH used as a modifier in R-PE/R-PA blends was evaluated by means of differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMTA), while the analysis of the chemical structure of this blend was carried out by Fourier transform infrared spectroscopy (FT-IR). The thermal properties, complex viscosity, and selected usage properties of R-PE/R-PA blends compatibilized with PE-g-MAH, i.e., density and water absorption, were evaluated. The morphology of the blends with and without the compatibilizer was observed by scanning electron microscopy. The R-PE/R-PA/MAH blend shows heterogenic structure, which is a result of the chemical reaction in reactive extrusion between functional groups of PE-g-MAH used as modifier and the end groups of R-PA6. The results show that the R-PE/R-PA blend with increased PE-g-MAH content showed increased hardness, stiffness, and ultimate tensile strength due to the increased degree of crystallinity. The increase in crystallinity is proportional to the improvement of the mechanical properties. Moreover, it is shown that 1 wt.% PE-g-MAH added to the R-PE/R-PA waste blend increases the interfacial interactions and compatibility between R-PE and R-PA, resulting in decreased polyamide particle size. Finally, the results show that it is possible to produce good quality regranulated products with advantageous properties and structure from immiscible polymer waste for industrial applications.

Przedstawiono współczesne problemy rynku opakowań z tworzyw sztucznych, wynikające ze zmian w ustawodawstwie Unii Europejskiej, wprowadzającym nowe podejście do gospodarki materiałami polimerowymi na każdym etapie ich cyklu życia. Opisano ideę Gospodarki o Obiegu Zamkniętym (GOZ, ang. Circular Economy) oraz rolę opakowań zrównoważonych w tym systemie. Przedstawiono najważniejsze zasady ekoprojektowania opakowań polimerowych w aspekcie ograniczenia powstawania odpadów i przydatności opakowań do odzysku na drodze recyklingu materiałowego. Ekoprojektowanie opakowań z tworzyw sztucznych ujęte w koncepcji Gospodarki o Obiegu Zamkniętym może wkrótce stać się istotnym czynnikiem przewagi konkurencyjnej w branży opakowaniowej.

This article proposes thermography as a non-contact diagnostic tool for assessing drive reliability. The application of this technique during the operation of the belt transmission with a heat-welded thermoplastic polyurethane V-belt was presented. The V-belt temperature changes depending on the braking torque load at different values of the rotational speed of the active pulley, which were adopted as diagnostic characteristics. In this paper, the surface morphology of the polyurethane (PU) belts was assessed on the basis of microscopic and hardness tests. A surface roughness tester was used to evaluate the surface wear. The surface morphology and topography of the materials was determined by scanning electron microscopy (SEM) and optical microscopy. It was found that the most favorable operating conditions occurred when the temperature values of active and passive connectors were similar and the temperature difference between them was small. The mechanical and structure results indicate that the wear of the PU belt was slight, which provided stability and operational reliability for V-belt transmission. The microscopic images lacked clear traces of cracks and scratches on the surface, which was confirmed by the SEM observations.

The article presents the potential impact of flat drive and transport belts on people’s safety during a fire. The analysis distinguished belts made of classically used fabric–rubber composite materials reinforced with cord and currently used multilayer polymer composites. Moreover, the products’ multilayers during the thermal decomposition and combustion can be a source of emissions for unpredictable and toxic substances with different concentrations and compositions. In the evaluation of the compared belts, a testing methodology was used to determine the toxicometric indicators (W_LC50SM) on the basis of which it was possible to determine the toxicity of thermal decomposition and combustion products in agreement with the standards in force in several countries of the EU and Russia. The analysis was carried out on the basis of the registration of emissions of chemical compounds during the thermal decomposition and combustion of polymer materials at three different temperatures. Moreover, the degradation kinetics of the polymeric belts by using the thermogravimetric (TGA) technique was evaluated. Test results have shown that products of thermal decomposition resulting from the neoprene (NE22), leder leder (LL2), thermoplastic connection (TC), and extra high top cower (XH) belts can be characterized as moderately toxic or toxic. Their toxicity significantly increases with the increasing temperature of thermal decomposition or combustion, especially above 450 °C. The results showed that the belts made of several layers of polyamide can be considered the least toxic in fire conditions. The TGA results showed that NBR/PA/PA/NBR belt made with two layers of polyamide and the acrylonitrile–butadiene rubber has the highest thermal stability in comparison to other belts.

This paper presents the contemporary problems of polymer waste recycling, mainly recycling cables from end-of-life vehicles. The authors developed a new material based on mixed polymer waste (ASR) modified with a ductile polymer, mainly recycled low-density polyethylene (rLDPE), to produce moisture-resistant boards with beneficial mechanical properties. The ASR-based compositions without and with homogenization process—including physical, chemical, and shear-assisted compatibilization—were successfully applied and verified by evaluating final recycled product properties. The results showed that recycled polyethylene (rLDPE) was effective as a modifier increasing tensile modulus and flexural strength compare to an ASR mixture. It was found that the adding 5 wt % of polyethylene-grafted maleic anhydride (PE-g-MAH) as a compatibilizer to the ASR mixture significantly increases the homogenization of the components in the ASR matrix. The optimal solution for management cable waste is the manufacture of ASR composites with homogenization using an internal mixer the adding 20 wt % of rLDPE and 5 wt % of PE-g-MAH to the mixed plastics cable waste. The results obtained demonstrate that the hot-pressing with the pre-blending with rLDPE and compatibilizer of the ASR based waste provides a high gain in mechanical and usage properties, enabling the circular economy of plastics from automotive cables.

The paper presents the results of the investigation into the themo-mechanical, rheological and structural properties of films made from recycled polyethylenes in the "foil-to-foil" system, the comparative material were films made from primary raw materials. The films were prepared by...