Spent coffee grounds (SCGs) have great potential as a useful, value-added biological material. In this context, activated carbon (AC) was prepared from SCGs by an activation process using H₃PO₄ at 600 °C in the air and used as an adsorbent for the azo dye AO7, a model molecule for dye colorants found in textile industry effluents. X-ray diffraction, SEM and BET revealed that the AC was predominantly amorphous, consisting of a powder of 20–100 µm particles with mesopores averaging 5.5 nm in pore size. Adsorption kinetics followed a pseudo-second-order law, while the Langmuir model best fitted the experimental isotherm data (maximum capacity of 119.5 mg AO7 per AC g). The thermodynamic parameters revealed that adsorption was endothermic and spontaneous. All the characterizations indicated that adsorption occurred by physisorption via mainly π–π interactions. The best experimental removal efficiency optimized by means of a Box–Behnken design and response surface methodology was 98% for an initial AO7 concentration of 20 mg·L⁻¹ at pH 7.5 with a dose of 0.285 g·L⁻¹ of AC and a contact time of 40 min. These results clearly show that activated carbon prepared from SCGs can be a useful material for efficiently removing organic matter from aqueous solutions.

Composite flat membranes were prepared using a dry uniaxial pressing process. The effect of the sintering temperature (850–950 °C) and smectite proportion (10–50 wt.%) on membrane properties, such as microstructure, mechanical strength, water permeability, and treatment performances, was explored. It was observed that increasing the sintering temperature and adding higher amounts of smectite increased the mechanical strength and shrinkage. Therefore, 850 °C was chosen as the optimum sintering temperature because the composite membranes had a very low shrinkage that did not exceed 5% with high mechanical strength, above 23 MPa. The study of smectite addition (10–50 wt.%) showed that the pore size and water permeability were significantly reduced from 0.98 to 0.75 µm and from 623 to 371 L·h⁻¹·m⁻²·bar⁻¹, respectively. Furthermore, the application of the used membranes in the treatment of indigo blue (IB) solutions exhibited an almost total turbidity removal. While the removal of color and COD decreased from 95% to 76%, respectively, they decreased from 95% to 52% when the amount of smectite increased. To verify the treated water’s low toxicity, a germination test was performed. It has been shown that the total germination of linseed grains irrigated by M_S10-Z90 membrane permeate was identical to that irrigated with distilled water. Finally, based on its promising properties, its excellent separation efficiency, and its low energy consumption, the M_S10-Z90 (10 wt.% smectite and 90 wt.% zeolite) sintered at 850 °C could be recommended for the treatment of colored industrial wastewater.

Ceramic membrane technology plays an important role in water and wastewater treatment. Strategic sourcing of various natural mineral resources has contributed to developing low-cost ceramic membranes. The combination with calcination of inorganic and organic wastes from domestic and agricultural activities results in fully sustainable ceramic membrane materials. In this work, ceramic membranes were developed using 96% clay, 2% almond shells and 2% lime. Sintering at 900, 950, and 1000 °C enabled the production of membranes (MK-900, MK-950, and MK-1000) in a clean, simple, and cost-effective manner. The average pore diameter and porosity decreased slightly from 44 to 42 nm and from about 30% to 26% with increasing sintering temperature, while the flexural strength increased from 25 to 40 MPa. The pure water permeability was 68 and 59 L·m⁻²·h⁻¹·bar⁻¹ for MK-900 and MK-950, respectively. Effective color (as Indigo blue) removal of 78% and 92% was observed for MK-900 and MK-950, respectively. More than 90% of the initial permeability was recovered after three cycles of dye filtration using water backwashing at each stage, indicating good fouling resistance of the prepared membranes.

Spent coffee grounds (SCG) have great potential as a useful, value-added biological material. In this context, activated carbon (AC) was prepared from SCG by an activation process using H3PO4 at 600°C in air and used as an adsorbent for the azo dye AO7, a model molecule for dye colorants found in textile industry effluents. X-ray diffraction, SEM and BET revealed that the AC was predominantly amorphous, consisting of a powder of 20-100 µm particles with mesopores averaging 5.5 nm in pore size. Adsorption kinetics followed a pseudo-second-order law, while the Langmuir model best fitted experimental isotherm data (maximum capacity of 119.5 mg AO7 per AC g). Thermodynamic parameters revealed that adsorption was endothermic and spontaneous. All the characterizations indicated that adsorption occurred by physisorption via mainly - interactions. The best experimental removal efficiency optimized by means of a Box-Behnken design and response surface methodology was 98% for an initial AO7 concentration of 20 mg.L-1 at pH 7.5 with a dose of 0.285 g.L-1 of AC and a contact time of 40 min. These results clearly show that activated carbon prepared from SCG can be a useful material for efficiently removing organic matter from aqueous solutions.