External quantum efficiency of industrial-grade green InGaN light-emitting diodes (LEDs) has been measured in a wide range of operating currents at various temperatures from 13 K to 300 K. Unlike blue LEDs, the efficiency as a function of current is found to have a multi-peak character, which could not be fitted by a simple ABC-model. This observation correlated with splitting of LED emission spectra into two peaks at certain currents. The characterization data are interpreted in terms of non-uniformity of the LED active region, which is tentatively attributed to extended defects like V-pits. We suggest a new approach to evaluation of temperature-dependent light extraction and internal quantum efficiencies taking into account the active region non-uniformity. As a result, the temperature dependence of light extraction and internal quantum efficiencies have been evaluated in the temperature range mentioned above and compared with those of blue LEDs.

We demonstrate a phosphor free, dichromatic GaN-based monolithic white LED with vertically stacked green and blue emitting multiple quantum wells. The optimal thickness of GaN barrier layer between green and blue quantum wells used is 8 nm. This device can be tuned over a wide range of correlated color temperature (CCT) to achieve warm white (CCT = 3600 K) to cool white (CCT = 13,000 K) emission by current modulation from 2.3 A/cm${}^2$ to 12.9 A/cm${}^2$. It is also demonstrated for the first time that a color rendering index (CRI) as high as 67 can be achieved with such a dichromatic source. The observed CCT and CRI tunability is associated with the spectral power evolution due to the pumping-induced carrier redistribution.