Currently, the significantly developing fields of tissue engineering related to the fabrication of polymer-based materials that possess microenvironments suitable to provide cell attachment and promote cell differentiation and proliferation involve various materials and approaches. Biomimicking approach in tissue engineering is aimed at the development of a highly biocompatible and bioactive material that would most accurately imitate the structural features of the native extracellular matrix consisting of specially arranged fibrous constructions. For this reason, the present research is devoted to the discussion of promising fibrous materials for bone tissue regeneration obtained by electrospinning techniques. In this brief review, we focus on the recently presented natural and synthetic polymers, as well as their combinations with each other and with bioactive inorganic incorporations in order to form composite electrospun scaffolds. The application of several electrospinning techniques in relation to a number of polymers is touched upon. Additionally, the efficiency of nanofibrous composite materials intended for use in bone tissue engineering is discussed based on biological activity and physiochemical characteristics.

The development of electrospun nanofibers based on cellulose and its derivatives is an inalienable task of modern materials science branches related to biomedical engineering. The considerable compatibility with multiple cell lines and capability to form unaligned nanofibrous frameworks help reproduce the properties of natural extracellular matrix and ensure scaffold applications as cell carriers promoting substantial cell adhesion, growth, and proliferation. In this paper, we are focusing on the structural features of cellulose itself and electrospun cellulosic fibers, including fiber diameter, spacing, and alignment responsible for facilitated cell capture. The study emphasizes the role of the most frequently discussed cellulose derivatives (cellulose acetate, carboxymethylcellulose, hydroxypropyl cellulose, etc.) and composites in scaffolding and cell culturing. The key issues of the electrospinning technique in scaffold design and insufficient micromechanics assessment are discussed. Based on recent studies aiming at the fabrication of artificial 2D and 3D nanofiber matrices, the current research provides the applicability assessment of the scaffolds toward osteoblasts (hFOB line), fibroblastic (NIH/3T3, HDF, HFF-1, L929 lines), endothelial (HUVEC line), and several other cell types. Furthermore, a critical aspect of cell adhesion through the adsorption of proteins on the surfaces is touched upon.

Hospital-acquired infections are considered a priority for public health systems since they pose a significant burden for society. High-touch surfaces of healthcare centers, including textiles, provide a suitable environment for pathogenic bacteria to grow, necessitating incorporating effective antibacterial agents into textiles. This paper introduces a highly durable antibacterial gel-like solution, Silver Shell™ finish, which contains chitosan-bound silver chloride microparticles. The study investigates the coating’s environmental impact, health risks, and durability during repeated washing. The structure of the Silver Shell™ finish was studied using transmission electron microscopy (TEM) and energy-dispersive X-ray spectroscopy (EDX). The TEM images showed a core–shell structure, with chitosan forming a protective shell around groupings of silver microparticles. The field-emission scanning electron microscopy (FESEM) demonstrated the uniform deposition of Silver Shell™ on the surfaces of the fabrics. AATCC Test Method 100 was employed to quantitatively analyze the antibacterial properties of the fabrics coated with silver microparticles. Two types of bacteria, Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli), were used in this study. The antibacterial results showed that after 75 wash cycles, a 100% reduction for both S. aureus and E. coli in the coated samples using crosslinking agents was observed. The coated samples without a crosslinking agent exhibited 99.88% and 99.81% reductions for S. aureus and E. coli after 50 washing cycles. To compare the antibacterial properties toward non-pathogenic and pathogenic strains of the same species, MG1655 model E. coli strain (ATCC 29213) and a multidrug-resistant clinical isolate were used. The results showed the antibacterial efficiency of the Silver ShellTM solution (up to 99.99% reduction) coated on cotton fabric. AATCC-147 was performed to investigate the coated samples’ leaching properties and the crosslinking agent’s effects against S. aureus and E. coli. All coated samples demonstrated remarkable antibacterial efficacy, even after 75 wash cycles. The crosslinking agent facilitated durable attachment between the silver microparticles and cotton substrate, minimizing the release of particles from the fabrics. Color measurements were conducted to assess the color differences resulting from the coating process. The results indicated fixation values of 44%, 32%, and 28% following 25, 50, and 75 washing cycles, respectively.

Nanoscale powders of hydrated Ca₂P₂O₇, CaCO₃, and a product of mixed-anionic composition containing P₂O₇⁴⁻ and CO₃²⁻ anions were synthesized from aqueous solutions of Ca(CH₃COO)₂, pyrophosphoric acid (H₄P₂O₇), and/or (NH₄)₂CO₃. Pyrophosphoric acid was previously obtained on the basis of the ion exchange process from Na₄P₂O₇ solution and H⁺-cationite resin for further introduction into the reactions as an anionic precursor. The phase composition of powders after the syntheses was represented by bioresorbable phases of X-ray amorphous hydrated Ca₂P₂O₇ phase, calcite and vaterite polymorphs of CaCO₃. Based on synthesized powders, simple cylindrical constructions were prepared via mechanical pressing and fired in the temperature range of 600–800 °C. Surface morphology observation showed the presence of bimodal porosity with pore sizes up to 200 nm and 2 μm, which is likely to ensure tight particle packing and roughness of the sample surface required for the differentiation of osteogenic cells. Thus, the prepared ceramic samples can be further examined as model objects for bone tissue repair.

The rapidly growing demand for cell manufacturing and in vitro tissue fabrication has led to the development of various technologies for biomimetic artificial extracellular matrix (ECM), including three major materials: hydrogels, fibrous scaffolds, and decellularized tissues. The latter two materials are closer to the biomimetic goal of replicating natural ECM. The scalability of the scaffolds made of decellularized tissues is limited. The development of 3D fibrous ECM is at the initial stage owing to the recent advantages of novel nanofiber spinning technologies. These novel technologies brought about simultaneous control over a range of critical characteristics, such as fiber diameter, length, material, draw ratio, spacing, and alignment into well-controlled 3D constructs. There is still a long way to go in designing 3D fibrous scaffolds based on cell response studies. The primary objective of this review is to provide an analysis of the recent progress in novel nano- and microfiber spinning methods and uncover their potential for precise fiber alignment into 3D structures.

The morphology of grown INS-1 cultures from spheroids to sheets is strongly affected by the properties of the 3D fiber scaffold.