Magnesium oxide is typically white and can be colorized with transition metal insertion by doping. We present the preparation of a green-colored hydroxide by the exchange of Mg²⁺ on the crystalline lattice with Ni²⁺ in MgO, using three nickel salts. MgO_st was prepared by the colloidal starch suspension method, using cassava starch. The oxides and hydroxides, before and after, were characterized by X-ray diffraction (XRD), and show that a phase change occurs: a transition from periclase (MgO) to brucite (Mg(OH)₂) due to the incorporation of nickel ions from different salts (acetate, chloride, and nitrate), resulting in the solid solution [Ni_xMg_1−x(OH)₂]. The FTIR spectrum corroborates the crystallographic structure identified through XRD patterns, confirming the formation of a crystal structure resembling brucite. The new samples present a green color, indicative of the incorporation of the Ni²⁺ ions. The antimicrobial activity of products resulting from the doping of magnesium oxide with nickel and the precursor MgO_st was assessed through the minimum inhibitory concentration (MIC) test. The evaluation included three bacterial strains: Staphylococcus aureus (ATCC 25923), Escherichia coli (ATCC 25922), Salmonella gallinarum (ATCC 9184), and a yeast strain, Candida albicans (ATCC 10231). The obtained results were promising; the tested samples exhibited antimicrobial activity, with a MIC ranging from 0.312 to 0.625 μg.μL⁻¹. The nickel compound, derived from the precursor chloride salt, demonstrated superior MIC activity. Notably, all tested samples displayed bactericidal activity against the S. aureus strain and exhibited a broad spectrum of inhibition, encompassing both Gram-positive and Gram-negative strains. Only the nickel compounds derived from precursors with acetate and nitrate anions demonstrated antimicrobial activity against C. albicans, exhibiting a fungistatic behavior. Based on the conducted studies, [Ni_xMg_1−x(OH)₂] has emerged as a promising antimicrobial agent, suitable for applications requiring the delay or inhibition of bacterial growth.

Magnesium oxide is typically white and can be colorized with transition metal insertion by doping or by adsorption. We present the preparation of green colored hydroxide by the adsorption of nickel ions by porous MgO. MgO was prepared by the colloidal starch suspension method and used to remove nickel ions from the aqueous solution. The oxides and hydroxides, before and after adsorption, were characterized by X-ray diffraction technical, and show that a phase change occurs, a transition from periclase (MgO) to brucite (Mg(OH)2) due to the interaction with nickel salts (acetate, chloride, and nitrate). The FTIR spectrum corroborates with the DRX data on the formation of brucite like crystal lattices. The new samples present a green color, indicative of the incor-po-ration of the Ni2+ ions. Mixed oxides in the form of brucite were used in microbiological tests and showed action against fungi and bacteria, with bactericidal, bacteriostatic, or fungistatic function. Green brucite (NixMg1-x(OH)2) can be used as an inorganic pigment in white or colorless paints with a special biocidal property.