This study aimed to synthesize magnesium oxide (MgO) using a colloidal starch method for two primary purposes: the removal of chromium (III) ions from synthetic wastewater and the subsequent use of the chromium-containing material as synthetic inorganic pigments (SIPs) in commercial paints. The synthesis used to obtain the oxide (St-MgO) is a promising method for using plants, such as cassava, as green fuels due to their abundance, low cost, and non-toxicity. With this, the oxide showed greater porosity and alkalinity, compared to commercial magnesium oxide (Cm-MgO). The MgO samples were subjected to structural characterization using XRD and FTIR, surface area and pore volume study by B.E.T. and SEM, and chemical composition by ICP-OES and thermogravimetric analysis (TGA). The crystalline periclase phase was identified for both samples, but the brucite phase was shown to be a secondary phase for the commercial sample. After the removal of chromium ions, the brucite crystalline phase became the majority phase for the samples, regardless of the concentration of ions removed. The pigments were characterized by color measurements and discussed in terms of colorimetric parameters using the CIELab method and electron spectroscopy (VIS-NIR). This study also evaluated the colorimetric stability of green pigments in aggressive environments (acidic and alkaline) over a 240 h exposure period, demonstrating minimal color difference. This study aims to develop materials for the decontamination of wastewater containing chromium and its reuse as a synthetic inorganic pigment, using an innovative and sustainable synthesis method.

In this study, raw smectite (Sm), from the Guarapuava–Parana–Brasil region, was saturated with copper ions (Cu-Sm) by ion exchange and the samples Sm and Cu-Sm were used in crystal violet (CV) adsorption and applied as an antimicrobial and antifungal hybrid pigment. Samples (Sm and Cu-Sm) were used to remove crystal violet (CV) dye from aqueous media, simulating wastewater. Samples after use as adsorbents were characterized and named smectite/adsorbed dye (Sm/Dye) and copper smectite/adsorbed dye (Cu-Sm/Dye); and they were applied as hybrid pigments with antimicrobial action. The Sm and Cu-Sm were characterized by X-ray diffractometry (XRD), energy dispersive X-ray fluorescence (EDXRF), vibrational spectroscopy (FTIR), Zeta potential (ζ), scanning electron microscopy (SEM), and colorimetry (CIE L*a*b*), enabling the identification of the presence of intercalated copper ions and on the smectite surface. The adsorption assays were carried out to evaluate the effects of initial dye concentration and contact time. Tests for application as a hybrid pigment showed good compatibility with commercial white paint being applied on plaster blocks and later photoaging and chemical stability tests were performed in acid and basic environments, both were discussed by colorimetry (CIE L*a*b*), thus being able to relate it to the color variation (∆E). The samples (Sm, Cu-Sm, Sm/Dye, and Cu-Sm/Dye) were dispersed in white paint at 10% and 20% (% w/w) to evaluate the ability to inhibit different microorganisms. The modification with copper ions promoted an increase in the adsorptive capacity relative to the raw smectite and provided antibacterial and antifungal action to the hybrid pigment against Escherichia coli, Staphylococcus aureus, Listeria monocytogenes, and Candida albicans. The Cu-Sm and Cu-Sm/Dye samples showed excellent results against all studied microorganisms and reveal successful materials that can be used in environments that require microbiological protection.

Magnesium oxide is typically white and can be colorized with transition metal insertion by doping. We present the preparation of a green-colored hydroxide by the exchange of Mg²⁺ on the crystalline lattice with Ni²⁺ in MgO, using three nickel salts. MgO_st was prepared by the colloidal starch suspension method, using cassava starch. The oxides and hydroxides, before and after, were characterized by X-ray diffraction (XRD), and show that a phase change occurs: a transition from periclase (MgO) to brucite (Mg(OH)₂) due to the incorporation of nickel ions from different salts (acetate, chloride, and nitrate), resulting in the solid solution [Ni_xMg_1−x(OH)₂]. The FTIR spectrum corroborates the crystallographic structure identified through XRD patterns, confirming the formation of a crystal structure resembling brucite. The new samples present a green color, indicative of the incorporation of the Ni²⁺ ions. The antimicrobial activity of products resulting from the doping of magnesium oxide with nickel and the precursor MgO_st was assessed through the minimum inhibitory concentration (MIC) test. The evaluation included three bacterial strains: Staphylococcus aureus (ATCC 25923), Escherichia coli (ATCC 25922), Salmonella gallinarum (ATCC 9184), and a yeast strain, Candida albicans (ATCC 10231). The obtained results were promising; the tested samples exhibited antimicrobial activity, with a MIC ranging from 0.312 to 0.625 μg.μL⁻¹. The nickel compound, derived from the precursor chloride salt, demonstrated superior MIC activity. Notably, all tested samples displayed bactericidal activity against the S. aureus strain and exhibited a broad spectrum of inhibition, encompassing both Gram-positive and Gram-negative strains. Only the nickel compounds derived from precursors with acetate and nitrate anions demonstrated antimicrobial activity against C. albicans, exhibiting a fungistatic behavior. Based on the conducted studies, [Ni_xMg_1−x(OH)₂] has emerged as a promising antimicrobial agent, suitable for applications requiring the delay or inhibition of bacterial growth.

Magnesium oxide is typically white and can be colorized with transition metal insertion by doping or by adsorption. We present the preparation of green colored hydroxide by the adsorption of nickel ions by porous MgO. MgO was prepared by the colloidal starch suspension method and used to remove nickel ions from the aqueous solution. The oxides and hydroxides, before and after adsorption, were characterized by X-ray diffraction technical, and show that a phase change occurs, a transition from periclase (MgO) to brucite (Mg(OH)2) due to the interaction with nickel salts (acetate, chloride, and nitrate). The FTIR spectrum corroborates with the DRX data on the formation of brucite like crystal lattices. The new samples present a green color, indicative of the incor-po-ration of the Ni2+ ions. Mixed oxides in the form of brucite were used in microbiological tests and showed action against fungi and bacteria, with bactericidal, bacteriostatic, or fungistatic function. Green brucite (NixMg1-x(OH)2) can be used as an inorganic pigment in white or colorless paints with a special biocidal property.