Nine samples of carbonate-free sodalite-group minerals, including those with abnormally high contents of polysulfide groups, fluoride anion and carbon dioxide molecules as well as synthetic fluoraluminate sodalite-type compound Na₈(Si₇Al₅O₂₄)(AlF₆)^3–·5H₂O, have been studied by means of electron microprobe analyses, infrared and Raman spectroscopy; the CO₂ content was determined using the selective sorption of gaseous ignition products. This article describes a semi-quantitative method for estimating the content of carbon dioxide molecules in these minerals, based on IR spectroscopy data. The data obtained demonstrate the existence of a sulfide sodalite-group mineral with the idealized formula Na₇(Si₆Al₆O₂₄)(S₃⁻)·H₂O, which differs significantly from the formula Na₆Ca₂(Si₆Al₆O₂₄)S^2–₂ accepted for lazurite. According to single-crystal X-ray structural analysis, in the F-rich sodalite-group mineral from the Eifel paleovolcanic region, Germany with the idealized formula Na₇(Si₆Al₆O₂₄)F⁻·nH₂O fluorine occurs as an isolated F⁻ anion, unlike synthetic F-rich sodalite-type compounds.

The Lavrion area corresponds to the western part of the Attic-Cycladic metamorphic belt, in the back-arc region of the active Hellenic subduction zone. Between the Eocene and the Miocene, metamorphic rocks (mainly marbles and schists) underwent several stages of metamorphism and deformation due to collision and collapse of the Cycladic belt. Exhumation during the Miocene was accommodated by the movement of a large-scale detachment fault system, which also enhanced emplacement of magmatic rocks, leading to the formation of the famous Lavrion silver deposits. The area around the mines shows the stacking of nappes, with ore deposition mainly localized within the marbles, at marble-schist contacts, below, within, or above the detachment. The Lavrion deposit comprises five genetically-related but different styles of mineralization, a feature never observed in another ore deposit elsewhere, containing the highest number of different elements of any known mining district. The local geology, tectonic, and magmatic activity were fundamental factors in determining how and when the mineralization formed. Other key factors, such as the rise and the fall of sea level, which resulted from climate change over the last million years, were also of major importance for the subsequent surface oxidation at Lavrion that created an unmatched diversity of secondary minerals. As a result, the Lavrion deposit contains 638 minerals of which Lavrion is type-locality for 23 of them, which is nearly 12% of all known species. Apart from being famous for its silver exploitation, this mining district contains more minerals than any other district on Earth. The unique geological, mineralogical, and educational (mining, archaeological, and environmental) features suggest that it is highly suitable to be developed as a future UNESCO Global Geopark.

Isomorphic substitutions of extra-framework components in sodalite-group aluminosilicate minerals and their thermal conversions have been investigated using infrared, Raman, electron spin resonance (ESR), as well as ultraviolet, visible and near infrared (UV–Vis–near IR) absorption spectroscopy methods and involving chemical and X-ray diffraction data. Sodalite-related minerals from gem lazurite deposits (haüyne, lazurite, and slyudyankaite) are characterized by wide variations in S-bearing extra-framework components including SO₄²⁻ and various polysulfide groups (S₂^●−, S₃^●−, S₄^●− radical anions, and S₄ and S₆ neutral molecules) as well as the presence of CO₂ molecules. Heating at 700 °C under reducing conditions results in the transformation of initial S-bearing groups SO₄²⁻ and S₃^●− to a mixture of S²⁻, HS⁻, S₂^●−, and S₄^●− and transformation of CO₂ to a mixture of CO₃²⁻ and C₂O₄²⁻ or HC₂O₄⁻ anionic groups. Further heating at 800 °C in air results in the decomposition of carbonate and oxalate groups, restoration of the SO₄²⁻ and S₃^●− groups, and a sharp transformation of the framework. The HS⁻ anion is stable only under reducing conditions, whereas the S₃^●− radical anion is the most stable polysulfide group. The HS⁻-dominant sodalite-group mineral sapozhnikovite forms a wide solid-solution series with sodalite. The conditions required for the formation of HS⁻- and CO₂⁰-bearing sodalite-group minerals are discussed.

A review of the crystal chemistry of Fe-deficient eudialyte-group minerals is given. Specific features of cation distribution over key sites in the crystal structure, including partial substitution of Fe²⁺ with Na, Mn and Zr at the M2 site are discussed. It is concluded that Na-dominant (at the M2 site) eudialyte-group members (^M2Na-EGMs) are markers of specific kinds of specific peralkaline (hyperagpaitic) igneous rocks and pegmatites. New data are obtained on the chemical composition, IR spectra and crystal chemistry for two samples of ^M2Na-EGMs with disordered M1 cations, which are a potentially new mineral species with the simplified formula (Na,H₂O)₁₅Ca₆Zr₃[Na₂(Fe,Zr)][Si₂₆O₇₂](OH)₂Cl·nH₂O.

New data on the isomorphism of extra-framework components (including chromophores) in two- and multilayer minerals belonging to the cancrinite and sodalite groups, are obtained using chemical and single-crystal X-ray diffraction data as well as infrared, Raman, ESR, UV–Vis–near IR absorption and photoluminescence spectroscopy methods. It is shown that the blue color of these minerals may be due to CO₃^•− or S₃^•− radical anions, whereas yellow and pink shadings are typically due to the presence of S₂^•− radical anions and S₄^•− or S₄, respectively. Two kyanoxalite varieties are distinguished: (1) with predominantly acid oxalate groups and (2) predominantly neutral oxalate groups. Zundel cation H₅O₂+ and CO₂ molecules are shown to be typical impurities in nosean. The Zundel cation is also detected in kyanoxalite and in the 12-layer, cancrinite-related mineral marinellite. Wide isomorphic series involving substitutions of SO₄⁻ for SO₃²⁻ and CO₃²⁻, as well as OH⁻ for H₂O and F⁻, are common for eight-layer, cancrinite-group minerals with an afghanite-type framework.