This paper proposes a new approach on the processing of silicon production waste (microsilica) as a raw material for metallurgical processing. It is known from practice that the granulometric composition of microsilica does not allow its use in metallurgical processing. The authors of this work propose its use together with a reductant as part of a briquetted charge. In this work, the optimal composition of the charge mixture for briquetting is determined. The main focus is on assessing the strength characteristics of the briquettes and analyzing their efficiency in the silicon smelting process. The strength of the briquettes was studied by the dropping method. As a result, in terms of strength and other characteristics, it is highly advisable to use briquettes consisting of 65% of microsilica and 35% special coke screenings. The obtained batches of high-strength briquettes were tested for the smelting of metallurgical grade silicon in a large-scale laboratory ore-thermal furnace to replace the traditional charge mixtures (high-quality quartzites, petroleum coke, wood chips, etc.) with briquettes. It was established that the briquetted monocharge ensures more intensive reduction processes and improves melting conditions compared to the traditional charge. This leads to higher silicon recovery rates, which was confirmed by tests, during which the maximum recovery rate reached 83.1% with a 30% replacement of the charge with briquettes. The batch of metallurgical silicon with 95-96% of Si content was obtained.

This work presents the results of optimizing the physicochemical properties of composite briquettes based on microsilica for metallurgical-grade silicon production. Microsilica, a waste product of silicon production, contains a sufficiently high amount of silicon dioxide (96-97%). This fact makes microsilica a promising composite material for metallurgical processing. However, its granulometric composition limits its direct use. The method of briquetting on an industrial briquetting press was used. The influence of the granulometric composition of the composite mixture on the heat tolerance and strength of the finished briquettes was studied. The methods of obtaining and testing the briquettes, their composition, and the briquetting and drying process are described. The obtained briquettes were tested for the smelting of metallurgical silicon. The silicon recovery rate in the metal with the standard charge was 71%, while the recovery rate with the briquetted monocharge was 85%. The results of silicon smelting from the briquettes demonstrated the high quality of the obtained metal, corresponding to the standards of metallurgical-grade silicon. The implementation of these technologies not only improves the quality of the final product but also addresses environmental issues related to the disposal of microsilica, reducing its accumulation and minimizing its impact on the environment.

This paper presents the results of optimizing the physicochemical properties of microsilica-based composite briquettes for metallurgical-grade silicon production. Microsilica, a waste product of silicon production, contains a sufficiently high amount of silicon dioxide (96–97%). This fact makes microsilica a promising composite material for metallurgical processing. However, its granulometric composition limits its direct use. The method of briquetting on an industrial briquetting press was used. The influence of the granulometric composition of the composite mixture on the heat tolerance and reactivity of the finished briquettes was studied. The methods of obtaining and testing the briquettes, their composition, and the briquetting and drying process were described. The obtained briquettes were tested for the smelting of metallurgical silicon. The silicon recovery rate in the metal with the standard charge was 71%, while the recovery rate with the briquetted monocharge was 85%. The results of silicon smelting from the briquettes demonstrated the high quality of the obtained metal, corresponding to the standards of metallurgical-grade silicon. The implementation of these technologies improves the quality of the finished product and addresses environmental issues related to the disposal of microsilica, reducing its accumulation and minimizing its impact on the environment.

This study investigates the thermodynamic and kinetic features of chromium reduction from chromium ore using complex Fe–Si–Cr and Al–Si–Cr alloys as reducing agents for the refined ferrochrome production. The thermodynamic probability of Cr₂O₃ reduction by silicon and aluminum was evaluated using thermodynamic equilibrium calculations based on reference thermodynamic data, including determination of the standard Gibbs free energy change over the studied temperature range. The results showed that both reduction routes are thermodynamically feasible, while aluminum exhibits a higher affinity for oxygen and a greater reducing capacity. The thermal behavior of chromium ore and its mixtures with Fe–Si–Cr and Al–Si–Cr alloys was studied by differential thermal and thermogravimetric analysis. The use of Al–Si–Cr, especially in briquetted form, was found to shift several thermal transformation stages to lower temperatures and to reduce the apparent activation energy of the high-temperature interaction stages compared with Fe–Si–Cr-containing mixtures. The obtained results indicate that Al–Si–Cr alloy is a promising complex reductant for intensifying chromium recovery and improving process conditions in refined ferrochrome production.