This study investigated the influence of diverse laser processing parameters on the thermophysical properties of Ti-6Al-4V and AlSi10Mg alloys manufactured via laser powder bed fusion. During fabrication, the laser power (50 W, 75 W, 100 W) and laser scanning speed (0.2 m/s, 0.4 m/s, 0.6 m/s) were adjusted while keeping other processing parameters constant. Besides laser processing parameters, this study also explored the impact of test temperatures on the thermophysical properties of the alloys. It was found that the thermophysical properties of L-PBF Ti-6Al-4V alloy samples were sensitive to laser processing parameters, while L-PBF AlSi10Mg alloy showed less sensitivity. In general, for the L-PBF Ti-6Al-4V alloy, as the laser power increased and laser scan speed decreased, both thermal diffusivity and conductivity increased. Both L-PBF Ti-6Al-4V and L-PBF AlSi10Mg alloys demonstrated similar dependence on test temperatures, with thermal diffusivity and conductivity increasing as the test temperature rose. The CALPHAD software Thermo-Calc (2023b), applied in Scheil Solidification Mode, was utilized to calculate the quantity of solution atoms, thus enhancing our understanding of observed thermal conductivity variations. A detailed analysis revealed how variations in laser processing parameters and test temperatures significantly influence the alloy’s resulting density, specific heat, thermal diffusivity, and thermal conductivity. This research not only highlights the importance of processing parameters but also enriches comprehension of the mechanisms influencing these effects in the domain of laser powder bed fusion.

Composite metal foam (CMF) is a new class of material based on a mixture of metal matrix composites and metal foams. While the mechanical properties of CMF are well studied, its thermal properties, particularly at extreme temperatures, are yet to be evaluated and established. This study investigates the specific heat capacity of stainless-steel composite metal foam at temperatures up to 1200 °C while comparing data obtained using the laser flash method and a differential scanning calorimetry method (DSC). Moreover, it outlines a detailed procedure for investigating the surface emissivity of composite metal foam (CMF) as a function of the emissivity of separate components (spheres and matrix). It uses experimental and analytical procedures to show how emissivity is directly affected by surface roughness, temperature, sphere curvature and viewing angles. The CMF used in this study consists of 316L stainless steel matrix and stainless-steel hollow spheres with varying sphere sizes.