Composite materials are the most common materials in use in modern dentistry. Over the years, the methods of photopolymerization of composite materials have been improved with the use of various devices, such as quartz tungsten halogen lamps (QTHs), light-emitting diode units (LEDs), plasma-arc lamps and argon-ion lasers. This study aimed to compare the mechanical properties of a composite material, depending on the time and mode of photopolymerization. One hundred and forty rectangular specimens (25 × 2 × 2 mm) and forty-two disc-shaped samples (5 mm diameter and 2 mm thickness) were prepared from shade A2 Boston composite resin. Samples were cured using the following seven photopolymerization protocols: four fast-cure modes (full power for 3, 5, 10, and 20 s), two pulse-cure modes (5 and 10 shots of 1 s exposures at full power), and one step-cure mode (soft start with a progressive cycle lasting 9 s). Specimens were subjected to a flexural strength test, Vickers microhardness test, and FTIR spectroscopy test. A 2-factor ANOVA and post-hoc tests were carried out to assess the differences in the flexural strength parameter between the tested groups of samples before and after aging. A mixed-model ANOVA was carried out to assess the differences in the Vickers microhardness parameter between the tested groups of samples before and after aging. The lowest values of flexural strength (p < 0.001) and Vickers microhardness (p < 0.001) were obtained for the 3 s mode for the pre- and post-aging groups. The FTIR mapping tests showed a much more homogeneous chemical structure of the composite after 20 s of continuous irradiation, compared to the sample irradiated for 5 s in the continuous mode. The mode and cure time affects the mechanical properties of the composite resin. Appropriate selection of the cure mode and time ensures better mechanical properties of composite resin. This suggests that the survival of dental restorations within the oral cavity could be extended by using longer photopolymerization durations.

Ion exchange technique as the reversible exchange of ions between the substrate and the surrounding medium can be an effective way of removing traces of ion impurities from the waters and wastewaters and obtaining a product of ultrapure quality. Therefore, it can be used in analytical chemistry, hydrometallurgy, purification and separation of metal ions, radioisotopes and organic compounds, and it also finds great application in water treatment and pollution control. In the presented paper, the new trends for ion exchanger characteristics determination and application are presented. Special attention is paid to the ion exchangers with multifunctionality for heavy metal ions removal. They show superior actions such as sorption capacity values with excellent resistance to fouling and the possibility of application in the co-current or modern packed bed counter-current systems, as well as for the condensate polishing or the conventional mixed bed systems in combination with other resins. The results of the paper are expected to help researchers to establish a powerful strategy to find a suitable ion exchanger for heavy metal ions removal from waters and wastewaters. It is important because the best ion exchangers are selected for a specific application during laboratory tests taking into account the composition of the feed solution, pH, type of ion exchangers and then the column breakthrough tests. Therefore, the optical profilometry and the X-ray photoelectron spectroscopy can prove beneficial for this purpose in the case of three different ion exchangers such as Dowex M 4195, Amberlite IRA 743 and Purolite Arsen X^np.

The paper presents the optimisation of a safe diode laser irradiation process applied to the surface of titanium implants in order to reduce microbial numbers in the treatment of inflammation classified as periimplantitis. The study comprised isolation and identification of microorganisms inhabiting surfaces of dental implants, crowns, teeth and saliva from patients with fully symptomatic periimplantitis. Microorganisms were detected by a culture-dependent method and identified with the use of MALDI-TOF mass spectrometry. The isolated microorganisms were inoculated on the surface of a new implant and then irradiated by a diode laser (wavelength of 810 ± 10 nm) in one, two or three repetitions and biocidal efficacy was assessed. To evaluate impact of laser irradiation on roughness, morphology and structure of the implant surface, optical profilometry, scanning electron microscopy and optical microscopy were used. Examination of the tested surfaces and saliva revealed the presence of Gram-positive and Gram-negative bacteria and one fungal species. In all patients, cultures from the endosseous part of the implant revealed the presence of the pathogenic and pyogenic bacterium Streptococcus constellatus. In 13 out of 20 samples laser-irradiated in duplicate and triplicate, all microorganisms were eliminated. The irradiation used did not cause any changes in the properties of the implant surface.

Defining the kidney stone composition is important for determining a treatment plan, understanding etiology and preventing recurrence of nephrolithiasis, which is considered as a common, civilization disease and a serious worldwide medical problem. The aim of this study was to investigate the morphology and chemical composition of multicomponent kidney stones. The identification methods such as infrared spectroscopy (FTIR), X-ray diffraction (XRD), and electron microscopy with the EDX detector were presented. The studies by the X-ray photoelectron spectroscopy (XPS) were also carried out for better understanding of their chemical structure. The chemical mapping by the FTIR microscopy was performed to show the distribution of individual chemical compounds that constitute the building blocks of kidney stones. The use of modern research methods with a particular emphasis on the spectroscopic methods allowed for a thorough examination of the subject of nephrolithiasis.

The paper presents the optimization of diode laser irradiation of corroded dental implants in order to reduce the number of microorganisms associated peri-implantitis. The research included the identification of microorganisms on the surface of removed dental implants in patients with peri-implantitis and the assessment of the biocidal effectiveness of the diode laser against these microorganisms. Laser desorption/mass spectrometry (MALDI-TOF MS) was used to identify microorganisms and metagens were examined by next generation sequencing (NGS). Irradiation was performed with a diode laser with a wavelength of λ = 810, operating mode: 25 W/15.000 Hz/10 μs, average = 3.84 W with the number of repetitions t = 2 × 15 s and t = 3 × 15 s. The structure and surface roughness of the implants were analysed before and after laser irradiation by optical profilometry and optical microscopy with confocal fixation. In total, 16 species of Gram-positive bacteria and 23 species of Gram-negative bacteria were identified on the surface of the implants. A total of 25 species of anaerobic bacteria and 12 species with corrosive potential were detected. After diode laser irradiation, the reduction in bacteria on the implants ranged from 88.85% to 100%, and the reduction in fungi from 87.75% to 96.77%. The reduction in microorganisms in the abutment was greater than in the endosseous fixture. The applied laser doses did not damage, but only cleaned the surface of the titanium implants. After 8 years of embedding, the removed titanium implant showed greater roughness than the 25-year-old implant, which was not exposed to direct influence of the oral cavity environment. The use of a diode laser in an optimised irradiation dose safely reduces the number of microorganisms identified on corroded dental implants in patients with peri-implantitis.

Polyester coatings are among the most commonly used types of powder paints and present a wide range of applications. Apart from its decorative values, polyester coating successfully prevents the substrate from environmental deterioration. This work investigates the cavitation erosion (CE) resistance of three commercial polyester coatings electrostatic spray onto AW-6060 aluminium alloy substrate. Effect of coatings repainting (single- and double-layer deposits) and effect of surface finish (matt, silk gloss and structural) on resistance to cavitation were comparatively studied. The following research methods were used: CE testing using ASTM G32 procedure, 3D profilometry evaluation, light optical microscopy, scanning electron microscopy (SEM), optical profilometry and FTIR spectroscopy. Electrostatic spray coatings present higher CE resistance than aluminium alloy. The matt finish double-layer (M2) and single-layer silk gloss finish (S1) are the most resistant to CE. The structural paint showed the lowest resistance to cavitation wear which derives from the rougher surface finish. The CE mechanism of polyester coatings relies on the material brittle-ductile behaviour, cracks formation, lateral net-cracking growth and removal of chunk coating material and craters’ growth. Repainting does not harm the properties of the coatings. Therefore, it can be utilised to regenerate or smother the polyester coating finish along with improvement of their CE resistance.