Carbonated hydroxyapatite derivatives (CHAp) and its metallic derivatives (Ag, Sr, Ba, K, Zn) have been prepared and characterized in this paper and their coating capacity on some model stone samples have been evaluated and discussed. These compounds were characterized by using several analytical tools, including X-ray diffraction analysis (XRD), thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), to determine the purity of the CHAp sample. The XRD and FTIR results confirmed the presence of AB-carbonated type CHAp. The thermal analysis (TGA) established two stages of weight loss that occured during the heating process: The first weight loss between 30–225 °C corresponding to the partial carbonate release from OH-channel and the second one between 226–700 °C, corresponding to some thermal reactions, possibly to the generation of calcium phosphate. The efficiency and suitability of these products on model stone samples were evaluated by monitoring the resistance to artificial weather (freeze–thaw), and pore structure changes (surface area, pore volume, pore diameter). Meanwhile, optical microscopy (OM) and Scanning Electron Microscopy with Energy Dispersive Spectroscopy (SEM–EDS) techniques showed the particles size and surface morphology of the samples, as well as information on its chemical composition. Also, the compressive strength of these new compounds as coatings revealed a homogeneity and strengthen of these model stone samples.

This study is the first attempt to decipher the effect of particulate matter (PM) composition on people’s health and on historic sites, in correlation with the daily and seasonal microclimate monitoring of the indoor and outdoor areas of the Roman Mosaic Edifice museum (the maritime port of Constanta, Romania). More specifically, the increase of metal concentrations in particulate matter during the summer of 2018 and spring of 2019 in the museum under investigation could possibly be associated with the microclimates of both seasons, with coastal factors, as well as with the anthropic activities specific to the port of Constanta. FTIR and inductively coupled plasma mass spectroscopy (ICP-MS) techniques, used for the investigation of PM_2.5–10 samples, revealed high concentrations of Fe, Al-rich, and soluble particles inside the investigated museum area. In this respect, the chemical measurements of the PM_2.5–10 masses highlighted high concentrations of heavy metals (i.e., Al, Fe, Zn, Mn, and Pb) and low concentrations of trace metals (i.e., Cr, Ni, Cu, and Cd). Statistical analysis showed that the chemical compositions of the particulate matter in the indoor and outdoor areas of the Roman Mosaic Edifice were influenced by microclimatic conditions, mainly temperature and relative humidity (RH). A potential health risk for tourists is the thermal and humid conditions, alongside the toxic components of the particulate matter. This research seeks to provide solutions for improving the environmental conditions inside the Roman Mosaic Edifice and to offer useful suggestions concerning health promotion and the protection of museum exhibits against possible future deterioration.

This research focuses on the synthesis of multi-walled carbon nanotubes (MWCNTs) decorated with TiO₂ nanoparticles (NPs) and incorporated in cellulose acetate-collagen film in order to obtain a new biomaterial with potential biomedical applications and improved antimicrobial activity. The successful decoration of the MWCNTs with TiO₂ NPs was confirmed by several structural and morphological analysis, such as Fourier transformed infrared spectroscopy, Raman spectroscopy, X-ray diffraction and transmission electron microscopy. The obtained nanocomposites were further incorporated into cellulose acetate-collagen films, at different concentrations and absorption kinetics, antimicrobial activity and in vitro biocompatibility of the obtained films was investigated. The antimicrobial tests sustained that the presence of the nanocomposites into the polymeric matrix is an important aspect in increasing and maintaining the antimicrobial activity of the polymeric wound dressings over time. The biocompatibility and cytotoxicity of the obtained films was evaluated using cellular viability/proliferation assay and fluorescent microscopy which revealed the ability of the obtained materials as potential wound dressing biomaterial.

AISI 316 steel has good corrosion behavior and high-temperature stability, but often prolonged exposure to temperatures close to 700 °C in aggressive environments (e.g., in boilers and furnaces, in nuclear installations) can cause problems that lead to accelerated corrosion degradation of steel components. A known solution is to prepare alumina ceramic coatings on the surface of stainless steel. The aim of this study is to obtain aluminum oxide ceramic coatings on 316L austenitic steel, by Plasma Electrolysis Oxidation (PEO), using a pulsed unipolar power supply. The structures obtained by PEO under various experimental conditions were characterized by XPS, SEM, XRD, and EDS analyses. The feasibility was proved of employing PEO in NaAlO₂ aqueous solution using a pulsed unipolar power supply for ceramic–like aluminum oxide films preparation, with thicknesses in the range of 20–50 μm, and a high content of Al₂O₃ on the surface of austenitic stainless steels.

A cost-effective solution to the problems that the automotive industry is facing nowadays regarding regulations on emissions and fuel efficiency is to achieve weight reduction of automobile parts. Glass fiber-reinforced polymers are regularly used to manufacture various components, and some parts may also contain thermoplastic elastomers for toughness improvement. This work aimed to investigate the effect of styrene-(ethylene-co-butylene)-styrene triblock copolymer (E) and treated fly ash (C) on the morphological, thermal, and mechanical properties of long glass fiber (G)-reinforced polypropylene (PP). Results showed that the composites obtained through melt processing methods presented similar thermal stability and improved (nano)mechanical properties compared to 25–30 wt.% G-reinforced PP composites (PP-25G/PP-30G). Specifically, the impact strength and surface hardness were greatly improved. The addition of 20 wt.% E led to a 25–39% increase in impact strength and surface elasticity, while the addition of 6.5 wt.% C led to a 16% increase in surface hardness. The composite based on 25 wt.% G, 6.5 wt.% C, and 20 wt.% E presented the best-balanced properties (8–17% increase in impact strength, 38–41% increase in axial strain, and 35% increase in surface hardness) compared with PP-30G/PP-25G. Structural and morphological analysis confirmed the presence of a strong interaction between the components that make the composites. Based on these results, the PP–G–E–C composites could be presented as a viable material for automotive applications.

(1) Background: Due to the precarious situation of many monuments or archeological sites, analytical investigations are necessary to obtain information about the used materials, as well as to identify the most appropriate solutions for their conservation/restoration. This paper addresses the characterization of mural painting fragments collected during the excavation in 2018 in Rapoltu Mare (La vie), Deva. (2) Methods: Specific analytical techniques were used, as follows: X-ray diffractometry (XRD), wavelength dispersive X-ray fluorescence (WDXRF), optical microscopy (OM), zoom microscopy and scanning electron microscopy (SEM), spectroscopic techniques (UV–Vis, FTIR, Raman), porosity and thermal analysis, all of which provide information about the structure, chemical composition, morphology and topography of pigments and their deterioration as well. (3) Results: Up to seven different pigments were identified: Egyptian blue, carbon, calcite, gypsum, hematite, goethite and green earth. Egyptian Blue is identified in all the other color areas, except the white area: in the green zone (as degradation product with beeswax) and in the red zone (in mixture with ochre) too. In addition, carbon and beeswax were highlighted as toner and binder for pigments, respectively. In the presence of the organic beeswax binding environment, the Egyptian blue pigment particles darkened or turned yellow significantly, changing the blue to a greenish color. It is also possible to identify wollastonite (CaSiO₃) in the blue pigment, which indicates that the temperature used in the manufacturing of Egyptian blue was higher than 950 °C from thermal analysis. The presence of apatite, hematite and gypsum deposits in the Hunedoara region certifies that these pigments could have been of local origin, as demonstrated by the presence of analytically identified elements (Fe, P, S, Ca). (4) Conclusions: The analytical techniques used for such investigations have highlighted the main pigments used in Roman times for various Roman murals.