To broaden the applications of wood, it is necessary to prepare flame-retardant coatings that can protect wood substrates during combustion. In this study, a bio-based, intumescent, flame-retardant phytic acid–melamine polyelectrolyte (PM) was prepared using phosphorus-rich biomass phytic acid and nitrogen-rich melamine as raw materials through an ion crosslinking reaction. Subsequently, a series of bio-based, flame-retardant wood coatings were prepared by optimizing the structure of urea–formaldehyde resin with the addition of melamine, sodium lignosulfonate, and PM as a flame-retardant curing agent. Woods coated with PM-containing coatings displayed significantly improved flame-retardant performances in comparison to uncoated woods. For PM-cured woods, the measured values of total heat release and total smoke production were 91.51% and 57.80% lower, respectively, compared with those of uncoated wood. Furthermore, the fire growth index decreased by 97.32%, indicating a lower fire hazard. This increase in flame retardancy and smoke suppression performance is due to the dense expanded carbon layer formed during the combustion of the coating, which isolates oxygen and heat. In addition, the mechanical properties of the flame-retardant coatings cured with PM are similar to those cured with a commercial curing agent, NH₄Cl. In addition, the prepared flame-retardant coating can also stain the wood. This study proves the excellent flame-retarding and curing effect of ammonium phytate in urea–formaldehyde resin coatings and provides a new approach for the application of bio-based flame retardants in wood coatings.

Urea–formaldehyde (UF) resin is the most widely used adhesive resin. However, it is necessary to improve its flame-retardant performance to expand its applications. In this study, exploiting electrostatic interactions, anionic phytic acid and cationic chitosan were combined to form a bio-based intumescent flame-retardant, denoted phytic acid–chitosan polyelectrolyte (PCS). The molecular structure of the urea–formaldehyde resin was optimized by crosslinking with melamine and plasticizing with polyvinyl alcohol-124. Thus, by combining PCS with the urea–formaldehyde resin and with ammonium polyphosphate and ammonium chloride as composite curing agents, flame-retardant urea–formaldehyde resins (FRUFs) were prepared. Compared to traditional UF resin, FRUF showed excellent flame retardancy and not only reached the UL-94 V-0 level, but the limit of oxygen index was also as high as 36%. Compared to those of UF, the total heat release and peak heat release rate of FRUF decreased by 86.44% and 81.13%, respectively. The high flame retardancy of FRUF originates from the combination of oxygen and heat isolation by the dense carbon layer, quenching of phosphorus free radicals, and dilution of oxygen by a non-flammable gas. In addition, the mechanical properties of the FRUF remained good, even after modification. The findings of this study provide a reference for the flame-retardant application of FRUF for applications in multiple fields.

In this study, environmentally friendly flame retardants capable of efficient flame retardancy at low concentrations in wood were developed. Urea-formaldehyde (UF) resin and guanidinium azole (GZ)-phytate (PA)-copper hydroxide (Cu(OH)₂) flame-retardant resin coating blends were prepared using urea, formaldehyde, 3,5-diamino-1,2,4-triazole (GZ), phytanic acid (PA), and copper hydroxide (Cu(OH)₂). Employing dioctyl phthalate as the plasticizer and tannic acid as the curing agent, a three-stage reaction was performed to obtain the desired UF-GZ/PA/Cu as a bio-based flame retardant. Thermal evaluations demonstrated that UF-GZ/PA/Cu lost 5% of its mass through decomposition at a temperature of 195.5 ± 2.1 °C, with its maximum decomposition rate being observed at 300.6 ± 1.5 °C, and 29.8 ± 2.5 wt.% of dense residual charcoal being obtained at 800 °C. When applied as a flame retardant coating on wood, the prepared UF-GZ/PA/Cu exhibited excellent flame-retardant properties, forming a continuous dense charcoal residual layer, with a limiting oxygen index of 32.0%, and passing the UL-94 V-0 test. In addition, the heat release rate and total heat release rate of the flame retardant were determined to be reduced by 87.7 and 83.66%, respectively. Overall, this study provides a green and effective method for the preparation of flame-retardant wood.

The issue of hazardous smoke and toxic gases released from epoxy resins (EP), which often causes casualties in real fires, has limited its application. Therefore, we have developed a novel flame retardant based on a bimetallic-doped phytate-melamine (BPM) structure with Zn²⁺ and Fe²⁺ ions incorporated into the polymer matrix using a straightforward solution-based synthetic method. The combustion performance of the composite was evaluated using a cone calorimeter test, which showed that the peak heat release, total heat release, and total smoke production were reduced by 50%, 31.7%, and 29.2%, respectively, compared to those of EP. Additionally, the fire growth index was noticeably reduced by 60% owing to the synergistic catalytic effect of the bimetallic ions, and the high nitrogen and phosphorus content of the additives. Overall, this study provides new insights into the application of bimetallic doping for flame retardant polymer composites.