Research on the application of graphene (G) and graphene quantum dots (GQDs) for biomedical engineering has attracted much attention over the last decade. Graphene and its derivatives have shown great biocompatibility, solubility, selectivity, large surface area, high purity, biofunctionalization, high drug loading capacity, and cell membrane penetration capability potential to be applied in biomedical engineering areas. The unique physical and chemical properties of GQDs, including small size, chemical inertness, high photoluminescence stability, low cytotoxicity, and good biocompatibility, made them a promising candidate for biomedical engineering applications. The recent progress related to the development of G and GQDs toward biomedical engineering applications is presented in this work. This study reviews and discusses the development of G and GQDs, both top-down and bottom-up synthesis methods, for biomedical engineering applications, such as biosensing, tissue engineering, drug delivery, bioimaging, antibacterial, and antiviral.

3D-printed nasopharyngeal swabs for medical sample collection have been manufactured via additive manufacturing (AM), evaluated, and characterized in the present study. A multi-part component of nasopharyngeal swabs was proposed, in which the swab and handle were manufactured separately to reach sustainable production and environmentally friendly products. The swab was investigated using tensile, flexural, surface roughness, dimensional accuracy, and sample collection testing. The influence of printing parameters and post-curing time treatment on the mechanical properties, surface roughness, and dimensional accuracy of 3D-printed nasopharyngeal swabs were also evaluated. The result showed that 3D-printed nasopharyngeal swab shows outstanding tensile strength compared to the commercial flock nasopharyngeal swab. Moreover, the swab neck flexibility test showed that both PLA and dental non-castable 3D-printed nasopharyngeal swabs were able to bend 180°. Subsequently, the surface roughness of 3D-printed nasopharyngeal swab was identic with the commercial flock nasopharyngeal swab. The proposed 3D-printed nasopharyngeal swab design could carry an artificial mucus sample of 141.6 mg at a viscosity of 9455.4 mPa.s. The cost to fabricate a 3D-printed nasopharyngeal swab was estimated at USD0.01–0.02 per swab. 3D-printed nasopharyngeal swab shows potential as a feasible option, greener, less medical waste, and more sustainable.

The study investigates the fabrication and analysis of nickel microparticle-reinforced composites fabricated using the digital light processing (DLP) technique. A slurry is prepared by incorporating Ni-micro particles into a resin vat; it is thoroughly mixed to achieve homogeneity. Turbidity fluctuations are observed, initially peaking at 50% within the first two minutes of mixing and then stabilizing at 30% after 15–60 min. FTIR spectroscopy with varying Ni wt.% is performed to study the alterations in the composite material’s molecular structure and bonding environment. Spectrophotometric analysis revealed distinctive transmittance signatures at specific wavelengths, particularly within the visible light spectrum, with a notable peak at 532 nm. The effects of printing orientation in the X, Y, and Z axes were also studied. Mechanical properties were computed using tensile strength, surface roughness, and hardness. The results indicate substantial enhancements in the tensile properties, with notable increases of 75.5% in the ultimate tensile strength and 160% in the maximum strain. Minimal alterations in surface roughness and hardness suggest favorable printability. Microscopic examination revealed characteristic fracture patterns in the particulate composite at different values for the wt.% of nickel. The findings demonstrate the potential of DLP-fabricated Ni-reinforced composites for applications demanding enhanced mechanical performance while maintaining favorable printability, paving the way for further exploration in this domain.