This study evaluated the stability and reusability of amino-functionalized nanocellulose aerogels as CO₂-adsorbent materials. The modified aerogels, synthesized via a controlled silylation using N-[3-(trimethoxysilyl) propyl] ethylenediamine (DAMO), demonstrated excellent thermal stability up to 250 °C (TGA) and efficient CO₂ adsorption through chemisorption, which was the main adsorption mechanism. The performance of the aerogels was assessed using both adsorption isotherms and the decay pressure technique, revealing that CO₂ adsorption capacity increased with higher amino group loading (4.62, 9.24, and 13.87 mmol of DAMO). At 298 K and 4 bar, CO₂ adsorption capacity increased proportionally with the amino group concentration, reaching values of 3.17, 5.98, and 7.86 mmol of CO₂ g⁻¹ polymer, respectively. Furthermore, over 20 adsorption/desorption cycles, the aerogels maintained 95% CO₂ desorption at ambient temperature, indicating their potential for industrial use. These findings highlight the aerogels suitability as stable, reusable materials for large scale CO₂ capture and storage technologies.

Bacterial nanocellulose (BNC) is a highly pure biopolymer with promising applications in the biomedical, food, and textile industries. However, the high production costs and low yields obtained in static conditions limit its scalability and industrial applications. This study addresses the sustainable production of BNC using a rotary disk bioreactor (RDB) and explores the use of grape pomace extract as an alternative carbon source for BNC production. Parameters such as the BNC production and biomass yield were evaluated using Komagataeibacter xylinus ATCC 53524 under different operational conditions (disk surface, rotation speed, and number of disks). The results showed that cellulose production increased using silicone-coated disks at 7–9 rpm (up to 2.72 g L⁻¹), while higher yields (5.23 g L⁻¹) were achieved when using grape pomace extract as the culture medium in comparison with conventional HS medium. FTIR and TGA characterizations confirmed that BNC obtained with grape pomace extract presents the same thermal and chemical characteristics than BNC produced with HS medium. This work provides insight into the feasibility of upscaling BNC production using a bioprocessing strategy, combining production in the RDB system and the use of an agro-industrial waste as a sustainable and cost-effective alternative.

This study evaluates the antimicrobial properties of nanocomposite materials based on polyvinyl alcohol (PVA) reinforced with cellulose nanofibrils (CNFs) and/or supplement-ed with biobased additives derived from blueberry pruning wastes, with the objective of developing biodegradable food packaging systems with antimicrobial properties. The nanocomposites were prepared using a solvent-casting processing approach, and their thermal, physicochemical, and antimicrobial properties were assessed. All the nanocomposites exhibited thermal stability up to 200 °C, confirming their suitabil-ity for conventional food packaging processing conditions. Antimicrobial activity tests re-vealed inhibitory effects against both Gram-positive and Gram-negative bacteria. Bleached PVA/CNFs films showed complete growth inhibition (100%) against E. coli and S. aureus. In contrast, unbleached PVA/CNFs and PVA/CNFsB supplemented with blueber-ry-derived additives exhibited selective inhibition against E. coli, highlighting the influ-ence of nanofibril composition and additive incorporation on antimicrobial performance. Zeta potential measurements revealed values of –35.3 mV for the CNFs, confirming their negatively charged surface, which may contribute to interactions with bacterial mem-branes. Additionally, scanning electron microscopy (SEM) showed that the incorporation of CNFs generates nanostructured surfaces with exposed fibrillar domains, where bacteri-al cells become adhered and immobilized. These topographical features suggest that the antimicrobial behavior of the nanocomposites is associated with direct bacteria–surface interactions, supporting a contact-active antimicrobial behavior associated with the CNFs.

In this study, a methacrylic derivative of xylan (XYLMA) was synthesized through transesterification reactions, with the aim of evaluating its physicochemical behavior and its interaction with kaolinite particles. Structural characterization by FT-IR and NMR spectroscopy confirmed the incorporation of methacrylic groups into the xylan (XYL) structure, with a degree of substitution of 0.67. Thermal analyses (TGA and DSC) showed a decrease in melting temperature and enthalpy in XYLMA compared to XYL, attributed to a loss of structural rigidity. Thermal analyses (TGA and DSC) revealed a decrease in the melting temperature and enthalpy of XYLMA compared to XYL, which is attributed to a loss of structural rigidity and a reduction in the crystalline order of the biopolymer. Aggregation tests in solution revealed that XYLMA exhibits amphiphilic behavior, forming micellar structures at a critical aggregation concentration (CAC) of 62 mg L⁻¹. In adsorption studies on kaolinite, XYL showed greater affinity than XYLMA, especially at acidic pH, due to reduced electrostatic forces and a greater number of hydroxyl groups capable of forming hydrogen bonds with the mineral surface. In contrast, modification with methacrylic groups in XYLMA reduced its adsorption capacity, probably due to the formation of supramolecular aggregates. These results suggest that interactions between xylan and kaolinite clay are key to understanding the role that hemicelluloses play in increasing copper recovery when added to flotation cells during the processing of copper sulfide ores with high clay content.

This study evaluated the stability and reusability of amino-functionalized nanocellulose aero-gels as CO₂ adsorbent materials. The modified aerogels, synthesized via a controlled silylation using N-[3-(trimethoxysilyl) propyl] ethylenediamine (DAMO), demonstrated excellent thermal stability up to 250°C (TGA) and efficient CO₂ adsorption through chemisorption, which was the main adsorption mechanism. The performance of the aerogels was assessed using both, adsorp-tion isotherms and the decay pressure technique, revealing that CO₂ adsorption capacity in-creased with higher amino group loading (4.62, 9.24, and 13.87 mmol of DAMO). At 298 K and 4 bar, CO₂ adsorption capacity increased proportionally with the amino group concentration, reaching values of 3.17, 5.98, and 7.86 mmol of CO₂ g-1 polymer, respectively. Furthermore, over 20 adsorption/desorption cycles, the aerogels maintained 95% CO₂ desorption at ambient tem-perature, indicating their potential for industrial use. These findings highlight the aerogels suitability as stable, reusable materials for large scale CO₂ capture and storage technologies.