This article presents the results of thermodynamic and experimental studies on the joint processing of a mixture of Shalkiya deposit zinc–lead sulfide ore and its concentration tailings in the presence of coke and magnetite. Using the HSC-6.0 software package, it was established by thermodynamic modeling that the silicon-containing products of the SiO₂ reduction in the system under consideration are FeSi, Si, Fe₃Si, Fe₅Si₃, FeSi₂, FeSi_2.33, and SiOg, which, based on the starting reduction temperature, form an increasing series: Fe₃Si (1200 °C); Fe₅Si₃, Si (1400 °C); and SiOg, FeSi₂, FeSi_2.33 (1500 °C). The smelting of the zinc–lead sulfide ore and concentration tailings mixture in the case of replacing 55% of the iron contained in the magnetite concentrate with steel shavings iron allowed us to produce FeSi45 ferrosilicon (41.9%–42.1% Si), with the extraction of 85% of the silicon in it, and sublimates containing 26.03% zinc and 13.47% lead, with the extraction of 97% of the zinc and 99% of the lead in them. In comparison with the initial ore-tailings mixture, the resulting sublimates are 11.83 times richer in zinc.

The article presents the results of thermodynamic and experimental research on the processing of cinders from the firing of Shalkiya deposit lead-zinc ore tailings with the production of siliceous ferroalloys. Thermodynamic modeling carried out using the HSC-6.0 complex based on the Gibbs energy minimization principle showed that the interaction occur with the formation of CaSiO3, FeSiO3, MgSiO3, K2OˑSiO2, FeSi, Fe5Si3, SiC, Fe3Si, Si, SiOg, FeSi2.33, FeSi2, CaSi, Zn, Zng, Pb, Pbg; an increase in the iron amount in the system allows increasing the silicon extraction degree into the alloy at 1800°C to 76%, to reduce the silicon concentration in the alloy from 41 to 24%; FS25 grade ferrosilicon formed at 1752-1867°C in the presence of 88-100% iron, and FS45 grade ferrosilicon – at 1863-1900°C and 20-22.4% iron. Electric melting of a charge containing 63.83% calcined cinder of tailings, 19.15% coke, and 17.02% steel chips allows to obtain FS45 grade ferrosilicon (44.1-43.9% Si) with the extraction of 69.7% silicon and sublimates with the content of 32-38% zinc and lead. The results obtained allow complex processing of lead-zinc sulfide ore tailings with the extraction of not only non-ferrous metals, but also silicon in the ferroalloy.

The article presents the results of thermodynamic prediction and electric smelting of Shalkiya sulfide zinc-lead-bearing ore in the presence of magnetite and coke. Using the HSC-6.0 software package, it was found that under equilibrium conditions in the presence of Fe3O4 and carbon, the reduction and formation of gaseous zinc from ZnS (according to ∆G° = 0) occurs at a temperature of 1205.7 °C, and the formation of ferroalloy at the interaction of the sulfide ore with magnetite and carbon begins at 1200 °C. About 58% of silicon is extracted into the ferroalloy at 1800–1900 °C; almost all zinc and 83–88% of lead turns into a gaseous state. Electric smelting of the sulfide ore in the presence of magnetite concentrate and coke makes it possible to obtain the FS45 grade ferrosilicon (42–43% of Si); the silicon extraction degree was 84–88%. At the same time, 97.3% of lead and 99.2% of zinc are extracted into the sublimates. The developed method for processing zinc sulfide ores allows us to increase the degree of raw materials' comprehensive use due to the extraction of not only zinc and lead, but also silicon. The technology can be used to process raw materials containing zinc, lead and silica, such as zinc ore concentration tailings.