In the context of the global energy structure transformation, concentrated solar power (CSP) technology has gained significant attention. Its future trajectory is oriented towards the construction of ultra-high temperature (700–1000 °C) power plants, aiming to enhance thermoelectric conversion efficiency and economic competitiveness. Chloride molten salts, serving as a crucial heat transfer and storage medium in the third-generation CSP system, offer numerous advantages. However, they are highly corrosive to metal materials. This paper provides a comprehensive review of the corrosion behaviors of stainless steels and high-temperature alloys in molten salts. It analyzes the impacts of factors such as temperature and oxygen, and it summarizes various corrosion types, including intergranular corrosion and hot corrosion, along with their underlying mechanisms. Simultaneously, it presents an overview of the types, characteristics, impurity effects, and purification methods of molten salts used for high-temperature heat storage and heat transfer. Moreover, it explores novel technologies such as alternative molten salts, solid particles, gases, liquid metals, and the carbon dioxide Brayton cycle, as well as research directions for improving material performance, like the application of nanoparticles and surface coatings. At present, the corrosion of metal materials in high-temperature molten salts poses a significant bottleneck in the development of CSP. Future research should prioritize the development of commercial alloy materials resistant to chloride molten salt corrosion and conduct in-depth investigations into related influencing factors. This will provide essential support for the advancement of CSP technology.

As concentrated solar power (CSP) systems evolve, the new generation of CSP systems will utilize chloride molten salts, which are cost-effective and have high operating temperatures, but are highly corrosive. In order to reduce the corrosiveness of chloride salts, we investigated the addition of different levels of Mg to chloride salts to study the effect on corrosion. In this paper, the corrosion behavior of 310S stainless steel with aluminum in high-temperature molten salt NaCl-KCl-MgCl₂ was studied. By adding different contents of magnesium corrosion inhibitor, the corrosion mechanism and the effect of the corrosion inhibitor were explored. The results show that the lowest corrosion rate of 6.623 mm/y was obtained for the aluminum-formed 310S with 0.05 wt.% Mg. However, the corrosion rate rises when the Mg content exceeds 0.05 wt.% compared to the corrosion rate of corroded specimens without Mg. Changing the added Mg content does not affect the corrosion products. For 310S stainless steel with aluminum, its corrosion inhibition was best achieved by adding 0.05 wt.% Mg to the chloride molten salt.

Concentrated solar power plant (CSP) technology holds significant application value in the renewable energy sector for converting solar radiation into thermal and electrical energy. As a heat storage medium for next-generation solar thermal power stations, chloride salts exhibit strong corrosive effects on structural components. To enhance corrosion resistance of the heated body in molten salt environments, Inconel 625 is modified by incorporating aluminum, which facilitates the formation of a protective oxide film. In this study, High-Aluminum Inconel 625, after cold rolling and solution treatment, was immersed in a NaCl-KCl-MgCl₂ eutectic chloride melt at 650 °C for 200 h. Post-corrosion analysis revealed the formation of an alumina layer on the surface, effectively mitigating corrosion. Increased aluminum content resulted in thicker alumina layers and the formation of oxidation products, such as Cr₂O₃, Fe₂O₃, MoO₂, and MgCr₂O₄ spinel structures, significantly enhancing the alloy’s corrosion resistance. The Inconel 625 cold-rolled plate with 5.31 wt% Al exhibited the best corrosion resistance (3510 μm/year), making it a promising candidate for use in next-generation CSP heat storage and exchange components.