As a member of smart materials, electrorheological elastomers (EREs) formed by pre-treating active electrorheological particles are attracting more and more attention. In this work, four Mg-doped strontium titanate particles with spherical, dendritic, flake-like and pinecone-like morphorlogies were obtained by hydrothermal and low-temperature co-precipitation. XRD, SEM, Raman and FT-IR were used to characterize the obtained products. The results showed that the sizes of Mg-doped strontium titanates are about 1.5‒2.0 μm, and the phase structure are dominated by cubic crystal. These Mg-doped strontium titanates were dispersed in a hydrogel composite elastic medium. Then, Mg-doped strontium titanate/glycerol/gelatin electrorheological composite hydrophilic elastomers were obtained with or without electric field. The electric field response properties of Mg-doped strontium titanate composite elastomers were investigated. It concluded that dendritic Mg-doped strontium titanate composite elastomers is high-performance EREs. And the maximum value of energy storage modulus of Mg-doped strontium titanate composite elastomers has achieved 8.70 MPa. This high electrorheological performance of the products is helpful for their applications in vibration control, force transducers, smart structures, dampers, and other fields.

As smart materials, electrorheological elastomers (EREs) formed by pre-treating active electrorheological particles are attracting more and more attention. In this work, four Mg-doped strontium titanate (Mg-STO) particles with spherical, dendritic, flake-like, and pinecone-like morphologies were obtained via hydrothermal and low-temperature co-precipitation. XRD, SEM, Raman, and FT-IR were used to characterize these products. The results showed that Mg-STOs are about 1.5–2.0 μm in size, and their phase structures are dominated by cubic crystals. These Mg-STOs were dispersed in a hydrogel composite elastic medium. Then, Mg-STO/glycerol/gelatin electrorheological composite hydrophilic elastomers were obtained with or without an electric field. The electric field response properties of Mg-doped strontium titanate composite elastomers were investigated. We concluded that dendritic Mg-STO composite elastomers are high-performance EREs, and the maximum value of their energy storage was 8.70 MPa. The significant electrorheological performance of these products is helpful for their applications in vibration control, force transducers, smart structures, dampers, and other fields.