Computer-aided design and computer-aided manufacturing (CAD/CAM) dentistry have significantly changed workflows in recent years. Restorations and devices can now be digitally designed and 3D-printed for dental care purposes. This clinical case report provides straightforward protocols for the digital design and 3D manufacture of gingivectomy and tooth preparation guides. These types of guides improved the gingival architecture of the anterior teeth and provided controllable tooth preparations prior to labial ceramic veneers. Thoughtful clinical evaluation started with listening to the patient’s chief complaint and extra- and intra-oral evaluations. Then a digital wax-up was performed, followed by an intra-oral mock-up, to evaluate the shape of the proposed restorations. After patient acceptance, the clinical procedure started with the gingivectomy and tooth preparation. Hand-crafted porcelain veneers were bonded under rubber dam isolation to avoid any contamination and maximize the bonding protocol. The esthetic and functional demands were fully satisfied. Predictable outcomes can be obtained whenever a meticulous evaluation and execution of all the steps are performed. Three dimensional printing technology allows the fabrication of devices such as gingivectomy and tooth reduction guides that help accomplish the desired results.

Background: This study aimed to evaluate the color stability of bulk-fill flowable resin composites with 2 difference shades at baseline and after artificial aging. Methods: Disk-shaped specimens (Ø10 × 4 mm) were fabricated from three bulk-fill flowable resin resin composites (Filtek Bulk-Fill Flow, Venus Bulk-Fill Flow, and Estelite Bulk-Fill Flow). The specimens in each bulk-fill resin composite group were divided into two subgroups (n = 10 per subgroup) with two different shades, A1 (N = 30) and A3 (N = 30), and were polymerized with light curing (800 mW/cm²/Valo LED Unit, Ultradent) and polished. The color difference between bulk-fill resin composites was evaluated at baseline and after artificial aging using a spectrophotometer (CM-700d, Konica Minolta, Tokyo, Japan) under D65 illumination. Color coordinates were measured with CIEDE2000, and color differences (∆E₀₀) and relative translucency parameter (RTP) values were calculated. Subsequently, the comparison of color changes (∆E₀₀) before and after thermocycling was performed using the t-test for paired samples. Results: The bulk-fill flow resin composites evaluated in the present study were capable of mimicking important optical properties such as light transmission. All the resin composites provided acceptable color stability at baseline and after thermocycling when the color A1 was used. On the other hand, whenever the shade A3 was used, the Venus Bulk-Fill Flow demonstrated the best optical properties. There was no statistically significant difference when comparing baseline and after thermocycling in bulk-fill flowable resin composites (p > 0.05). After thermocycling, A1 bulk-fill flowable resin composites provided acceptable color stability, and all A3 bulk-fill flowable resin composites provided visible color change, except for the Venus Bulk-Fill Flow (∆E₀₀ = 2.35). Conclusions: Estelite Bulk-Fill Flow displayed the best color stability (∆E₀₀ = 2.22) between all the combinations evaluated.