Implants are readily applied as a convenient method of therapy. There is great interest in the prolonged release of active substances from implants. The objective of this work was to evaluate the dissolution kinetics of steroidal anti-inflammatory preparation (SAP) released from novel implants, and to test the influence of the technology on SAP release kinetics. The proposed long-acting preparations may overcome difficulties resulting from repeated injections and often visits to ambulatory clinic, as the stabilizing function of the artificial ligament would be enriched with pharmacological activity. The potential advantages provided by the new coatings of knee implants include the continuous, sustained, and prolonged release of an active substance. The study was carried out using a modified United States Pharmacopoeia (USP) apparatus 4. The amount of SAP was measured spectroscopically. It was revealed that the transport of the drug was mainly a diffusion process. The drug release kinetics was analyzed using zero-, first-, and second-order kinetics as well as Korsmeyer-Peppas, Higuchi, and Hixon-Crowell models. The highest values of the release rate constants were k₀ = (7.49 ± 0.05) × 10⁻⁵ mg × min⁻¹, k₁ = (6.93 ± 0.05) × 10⁻⁶ min⁻¹, and k₂ = (7.70 ± 0.05) × 10⁻⁷ mg⁻¹ × min⁻¹ as calculated according to zero-, first-, and second-order kinetics equations, respectively. The values of the rate constants obtained for the slowest process were k₀ = (3.63 ± 0.06) × 10⁻⁵ mg × min⁻¹, k₁ = (2.50 ± 0.03) × 10⁻⁶ min⁻¹, and k₂ = (2.80 ± 0.03) × 10⁻⁷ mg⁻¹ × min⁻¹. They may suggest the possibility of sustained release of betamethasone from the system. Due to the statistical analysis, differences were observed between most of the studied implants. Incubation, temperature, time of stabilization of layers, and the method of SAP deposition on the matrix affected the drug release.

In this study, metal-based biomaterials were functionalized with ascorbic acid (LAA). Two types of substrates were used: austenitic steel 316L and titanium Ti6Al4V. Coatings were prepared with the sol-gel method and applied on metal surfaces using the dip-coating technique. Ascorbic acid was delivered with SiO2-coating at concentrations of 0.1 and 0.4 M. The morphology of the surfaces and coatings was determined using scanning electron microscope (SEM), whereas their elemental composition by SEM-EDX. Immobilization of ascorbic acid in the coatings was confirmed with Raman spectroscopy. The biocompatibility of the materials obtained was tested in vitro using both bone marrow- and adipose-derived mesenchymal stem cells (BMMSC and ADMSC, respectively). Proliferation rate and morphology of cells cultured in the presence of designed biomaterials were monitored after 24, 48, 120 and 168 h of propagation. The results obtained indicated that silica coatings doped with 0.4 M LAA had a positive effect on the proliferation rate of investigated cells, and in some cases on the growth pattern of culture.

Corrosion is constantly a major problem of the world economy in the field of metal products, metal processing and other areas that utilise metals. Previously used compounds utilizing hexavalent chromium were amongst the most effective materials for corrosion protection but regulations have been recently introduced that forbid their use. Consequently, there is a huge drive by engineers, technologists and scientists from different disciplines focused on searching a new, more effective and environmentally-friendly means of corrosion protection. One novel group of materials with the potential to solve metal protection problems are sol-gel thin films, which are increasingly interesting as mitigation corrosion barriers. These environmentally-friendly and easy-to-obtain coatings have the promise to be an effective alternative to hexavalent chromium compounds using for anti-corrosion industrial coatings. In this review the authors present a range of different solutions for slow down the corrosion processes of metallic substrates by using the oxides and doped oxides obtained by the sol-gel method. Examples of techniques used to the sol-gel coating examinations, in terms of anti-corrosion protection, are also presented.

The objective of this study was to determine biocompatibility of zirconia-based coatings obtained by the sol–gel method. Two matrices, ZrO₂ and SiO₂/ZrO₂, were created and applied on stainless steel type 316L with dip-coating technique. The morphology and topography of biomaterials’ surface were characterized using energy-dispersive X-ray spectroscopy and atomic force microscopy, while chemical composition was analyzed by Raman spectroscopy. Additionally, wettability and surface free energy were characterized. Biocompatibility of obtained biomaterials was evaluated using an in vitro model employing mesenchymal stem cells (MSCs) of adipose and bone marrow origin. Biological analysis included determination of proliferation activity and morphology of MSCs in cultures on synthesized biomaterials. Osteoinductive properties of biomaterials were determined both in non-osteogenic, as well as osteogenic conditions. The results showed that investigated biomaterials exerted different impact on MSCs. Biomaterial with ZrO₂ layer was more biocompatible for adipose-derived MSCs, while SiO₂/ZrO₂ layer promoted proliferation of bone marrow derived MSCs. Moreover, hybrid coating exhibited greater osteoinductive properties than ZrO₂ coating, both on cultures with adipose-derived stromal (stem) cells and bone marrow stromal cells. Observed biological effects may result not only from different chemical composition, but also from diverse wettability. The ZrO₂ coating was characterized as hydrophobic layer, while SiO₂/ZrO₂ exhibited hydrophilic properties. The results obtained suggest that behavior of MSCs in response to the biomaterial may vary depending on their origin, therefore we postulate, that screening analysis of implants’ biocompatibility, should incorporate model applying both adipose- and bone marrow derived MSCs.