In this work, new co- and ter-polymers of methyl methacrylate (MMA), ethyl methacrylate (EMA), and N-butyl methacrylate (nBuMA), containing just 1% mol × mol⁻¹ of a fluorinated co-monomer, 3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluoro-octyl methacrylate (POMA), were synthesized. After an UV accelerated aging test, the photo-chemical stability of the polymers prepared was determined by ¹H NMR and FT-IR spectroscopy, size exclusion chromatography, differential scanning calorimetry and wettability measurements. The polymers were applied to Botticino tiles to achieve better performances in terms of water repellency and consequently deterioration resistance. One-year prolonged exposure to a real environment was conducted and the properties of the coated materials and their performances were studied using different surface techniques such as water contact angle (WCA) and colorimetric measurements (CIELaB), capillary absorption, permeability (RVP) tests and soluble salts determination. The effectiveness of the fluorinated methacrylic coatings was clearly demonstrated; among all the resins, the co-polymer MMA_POMA seems to be the most performing one. Furthermore, both the UV photo-chemical resistance and the easiness of removal was successfully studied.

Polyamide 6 (PA6) suffers from fast degradation in humid conditions due to hydrolysis of amide bonds, which limits its durability. The addition of nanotubular fillers represents a viable strategy for overcoming this issue, although the additive/polymer interface at high filler content can become privileged site for moisture accumulation. As a cost-effective and versatile material, halloysite nanotubes (HNT) were investigated to prepare PA6 nanocomposites with very low loadings (1–45% w/w). The roles of the physicochemical properties of two differently sourced HNT, of filler functionalization with (3-aminopropyl)triethoxysilane and of dispersion techniques (in situ polymerization vs. melt blending) were investigated. The aspect ratio (5 vs. 15) and surface charge (−31 vs. −59 mV) of the two HNT proved crucial in determining their distribution within the polymer matrix. In situ polymerization of functionalized HNT leads to enclosed and well-penetrated filler within the polymer matrix. PA6 nanocomposites crystal growth and nucleation type were studied according to Avrami theory, as well as the formation of different crystalline structures (α and γ forms). After 1680 h of ageing, functionalized HNT reduced the diffusion of water into polymer, lowering water uptake after 600 h up to 90%, increasing the materials durability also regarding molecular weights and rheological behavior.