Highly efficient air filtration with low pressure drop is the key to air purification. In this work, a self-powered electrospun nanofiber membrane with an electrostatic adsorption effect was prepared to improve the filtration efficiency of micro/nano particles. The composite membrane was comprised of polyvinyl chloride (PVC) nanofibers and polyamide-6 (PA6) nanofibers. The triboelectric effect between the two adjacent nanofiber membranes generated electrostatic charges under the action of air vibration, by which the electrostatic adsorption with the same pressure drop was enhanced. The electrostatic voltage on the self-powered nanofiber membrane was 257.1 mV when the flow velocity was 0.1 m/s. For sodium chloride (NaCl) aerosol particles with a diameter of 0.3 μm, the removal efficiency of the self-powered composite nanofiber membrane was 98.75% and the pressure drop was 67.5 Pa, which showed a higher quality factor than the membrane without electrostatic charges. This work provides an effective way to improve the filtration performance of air filter membranes.

The stable and continuous ejection of multiple jets with high densities is the key to the application of electrospinning technology. An arced multi-nozzle spinneret was designed to increase the production efficiency of electrospinning. The distribution of the electrical field was simulated to optimize the nozzles’ distribution of the spinneret. When the nozzles were arranged in an arc array, a relatively uniform electrical field could be obtained, which was beneficial for the weakening of electrical interference among the nozzles. Under the optimized electrical field, multiple jets from each nozzle could be ejected in a stable and continuous way. With the increase of the applied voltage, the electrical stretching force became larger, and there were fewer bonding structures. The average diameter of the electrospun nanofibers decreased with the increase of the applied voltage. When the distance between the inner nozzle and the collector increased, the charged jets suffered a larger stretching effect, resulting in the decrease of the average diameter of the electrospun nanofibers. The electrospinning current increased with the applied voltage and decreased with the distance between the inner nozzle and the collector, which is an important aspect for the monitoring of electrospinning jets. This work provides an effective way to promote the production efficiency of electrospun nanofibrous membranes.