Highly efficient air filtration with low pressure drop is the key to air purification. In this work, a self-powered electrospun nanofiber membrane with an electrostatic adsorption effect was prepared to improve the filtration efficiency of micro/nano particles. The composite membrane was comprised of polyvinyl chloride (PVC) nanofibers and polyamide-6 (PA6) nanofibers. The triboelectric effect between the two adjacent nanofiber membranes generated electrostatic charges under the action of air vibration, by which the electrostatic adsorption with the same pressure drop was enhanced. The electrostatic voltage on the self-powered nanofiber membrane was 257.1 mV when the flow velocity was 0.1 m/s. For sodium chloride (NaCl) aerosol particles with a diameter of 0.3 μm, the removal efficiency of the self-powered composite nanofiber membrane was 98.75% and the pressure drop was 67.5 Pa, which showed a higher quality factor than the membrane without electrostatic charges. This work provides an effective way to improve the filtration performance of air filter membranes.

The stable and continuous ejection of multiple jets with high densities is the key to the application of electrospinning technology. An arced multi-nozzle spinneret was designed to increase the production efficiency of electrospinning. The distribution of the electrical field was simulated to optimize the nozzles’ distribution of the spinneret. When the nozzles were arranged in an arc array, a relatively uniform electrical field could be obtained, which was beneficial for the weakening of electrical interference among the nozzles. Under the optimized electrical field, multiple jets from each nozzle could be ejected in a stable and continuous way. With the increase of the applied voltage, the electrical stretching force became larger, and there were fewer bonding structures. The average diameter of the electrospun nanofibers decreased with the increase of the applied voltage. When the distance between the inner nozzle and the collector increased, the charged jets suffered a larger stretching effect, resulting in the decrease of the average diameter of the electrospun nanofibers. The electrospinning current increased with the applied voltage and decreased with the distance between the inner nozzle and the collector, which is an important aspect for the monitoring of electrospinning jets. This work provides an effective way to promote the production efficiency of electrospun nanofibrous membranes.

Electrospray is a simple and cost-effective method to fabricate micro-structured thin films. This work investigates the electrospray process of ZnO patterns. The effects of experimental parameters on jet characteristics and electrosprayed patterns are studied. The length of stable jets increases with increasing applied voltage and flow rate, and decreases with increasing nozzle-to-substrate distance, while electrospray angles exhibit an opposite trend with respect to the stable jet lengths. The diameter of electrosprayed particles decreases with increasing applied voltage, and increases with flow rate. Furthermore, an alcohol gas sensor is presented. The ZnAc is calcined into ZnO, which reveals good repeatability and stability of response in target gas. The sensing response, defined as the resistance ratio of R₀/R_g, where R₀ and R_g are resistance of ZnO in air and alcohol gas, increases with the concentration of alcohol vapors and electrospray deposition time.

High-performance air filtration was the key to health protection from biological and ultrafine dust pollution. A self-supporting, three-dimensional (3D) nanofibrous membrane with curled pattern was electrospun for the filtration, of which the micro-fluffy structure displayed high-filtration efficiency and low-pressure drop. The flow field in the 3D filtration membrane was simulated to optimize the process parameters to increase the filtration performance. The qualification factor increased from 0.0274 Pa⁻¹ to 0.0309 Pa⁻¹ by 12.77% after the optimization of the electrospinning parameters. The best filtration efficiency and pressure drop were 93.6% and 89.0 Pa, separately. This work provides a new strategy to fabricate 3D structures through the construction of fiber morphology and promotes further improvement of air filtration performance of fibrous filters.

Electrohydrodynamic direct-writing (EDW) is a developing technology for high-resolution printing. How to decrease the line width and improve the deposition accuracy of direct-written patterns has been the key to the promotion for the further application of EDW. In this paper, an airflow-assisted spinneret for electrohydrodynamic direct-writing was designed. An assisted laminar airflow was introduced to the EDW process, which provided an additional stretching and constraining force on the jet to reduce the surrounding interferences and enhance jet stability. The flow field and the electric field around the spinneret were simulated to direct the structure design of the airflow-assisted spinneret. Then, a series of experiments were conducted, and the results verified the spinneret design and demonstrated a stable ejection of jet in the EDW process. With assisted airflow, the uniformity of printed patterns and the deposition position accuracy of a charged jet can be improved. Complex patterns with positioning errors of less than 5% have been printed and characterized, which provide an effective way to promote the integration of micro/nanosystems.

Mass loading of functional particles on the surface of nanofibers is the key to efficient heavy metal treatment. However, it is still difficult to prepare nanofibers with a large number of functional particle loads on the surface simply and efficiently, which hinders the further improvement of performance and increases the cost. Here, a new one-step strategy was developed to maximize the adhesion of graphene oxide (GO) particle to the surface of polyvinylidene fluoride (PVDF) nanofibers, which was combined with coaxial surface modification technology and blended electrospinning. The oxygen content on the as-prepared fiber surface increased from 0.44% to 9.32%, showing the maximized GO load. The increased adsorption sites and improved hydrophilicity greatly promoted the adsorption effect of Cr(VI). The adsorption capacity for Cr(VI) was 271 mg/g, and 99% removal rate could be achieved within 2 h for 20 mL Cr(VI) (100 mg/L), which was highly efficient. After five adsorption–desorption tests, the adsorption removal efficiency of the Cr(VI) maintained more than 80%, exhibiting excellent recycling performance. This simple method achieved maximum loading of functional particles on the fiber surface, realizing the efficient adsorption of heavy metal ions, which may promote the development of heavy-metal-polluted water treatment.