Nanocrystalline Cellulose (NCC or CNC) is widely used as a filler in polymer composites due to its high specific strength, tensile modulus, aspect ratio, and sustainability. However, CNC hydrophilicity complicates its dispersion in hydrophobic polymeric matrices giving rise to aggregate structures and thus compromising its reinforcing action. CNC functionalization in a homogeneous environment, through silanization with trichloro(butyl)silane as a coupling agent and subsequent grafting with bio-based polyols, is herein investigated aiming to enhance CNC dispersibility improving the filler-matrix interaction between the hydrophobic PU and hydrophilic CNC. The modified CNCs (m_Ci) have been studied by XRD, SEM, and TGA analyses. The TGA results show that the amount of grafted polyol is strongly influenced by both its molar mass and OH number and the maximum amount of grafted polyol reaches up to 0.32 mmol per grams of functionalized CNC, within the explored conditions. The effect of different concentrations (1-3 wt%) of m_Ci on the physical, morphological, and mechanical properties of the resulting bio-based composite polyurethane foams is evaluated. Composite PU foams present compressive modulus up to 4.81 MPa and strength up to 255 kPa more than five times higher than those reinforced with unmodified CNC or with modified CNC in heterogeneous chemical environment. The improvement of mechanical properties of the examined PU foams, as a consequence of the incorporation of bio-polyols modified CNCs where polyol's OH groups interact with polyurethane precursors, could further broaden the use of these materials in building applications.

In the last century, the issue of “water reserves” has become a remarkably strategic topic in modern science and technology. In this context, water resource treatment and management systems are being developed in both agricultural and urban area scenarios. This can be achieved using superabsorbent polymers (SAPs), highly cross-linked hydrogels with three-dimensional, hydrophilic polymer structures capable of absorbing, swelling and retaining huge amounts of aqueous solutions. SAPs are able to respond to several external stimuli, such as temperature, pH, electric field, and solution composition and concentration. They can be used in many areas, from sensor technology to drug delivery, agriculture, firefighting applications, food, and the biomedical industry. In addition, new categories of functional SAP-based materials, mainly superabsorbent polymer composites, can also encapsulate fertilizers to efficiently provide the controlled release of both water and active compounds. Moreover, SAPs have great potential in wastewater treatment for the removal of harmful elements. In this respect, in the following review, the most promising and recent advances in the use of SAPs and composite SAPs as tools for the sustainable management and remediation of water resource are reviewed and discussed by identifying opportunities and drawbacks and highlighting new challenges and aims to inspire the research community.

To obtain sustainable food packaging materials, alternatives to traditional ones must be researched. In this work, two different kinds of zeolites, i.e., a natural one, Clinoptilolite, and a synthetic one, Zeolite Na-X, were mixed with thermoplastic polyurethane for the fabrication of composites. Composite films were prepared via a hot mixing stage and then by means of a hot compression molding process. Several TPU/zeolite composites were produced with a filler concentration ranging from 5% to 10%wt. Finally, the obtained films were characterized by Fourier Transform Spectroscopy (FT-IR, ATR), thermal analysis (TGA and DSC), frequency sweep test, scanning electron microscopy (SEM), mechanical tensile test and oxygen permeability test. For both fillers and at all concentrations, the inclusion of zeolites significantly influenced the analyzed properties. In the TPU/zeolite composites, an overall enhancement was observed compared to the neat polymer, attributed to improved processability, superior barrier properties and the potential to create active materials by loading zeolite combined with various chemicals for specific applications. These findings suggest that the resulting composites hold considerable promise for applications in the food packaging sector.