A new approach regarding the development of nanostructured V₂O₅ electrochromic thin films at low temperature (250 °C), using air-carrier spray deposition and ammonium metavanadate in water as precursor is presented. The obtained V₂O₅ films were characterized by X-ray diffraction, scanning electron microscopy and Raman spectroscopy, while their electrochromic response was studied using UV-vis absorption spectroscopy and cyclic voltammetry. The study showed that this simple, cost effective, suitable for large area deposition method can lead to V₂O₅ films with large active surface for electrochromic applications.

The present communication reports on the effect of the sprayed solution volume variation (as a thickness variation element) on the detailed Raman spectroscopy for WO₃ thin films with different thicknesses grown from precursor solutions with two different concentrations. Walls-like structured monoclinic WO₃ thin films were obtained by the spray deposition method for further integration in gas sensors. A detailed analysis of the two series of samples shows that the increase in thickness strongly affects the films’ morphology, while their crystalline structure is only slightly affected. The Raman analysis contributes to refining the structural feature clarifications. It was observed that, for 0.05 M precursor concentration series, thinner films (lower volume) show less intense peaks, indicating more defects and lower crystallinity, while thicker films (higher volume) exhibit sharper and more intense peaks, suggesting improved crystallinity and structural order. For higher precursor concentration 0.1 M series, films at higher precursor concentrations show overall more intense and sharper peaks across all thicknesses, indicating higher crystallinity and fewer defects. Differences in peak intensity and presence reflect variations in film morphology and structural properties due to increased precursor concentration. Further studies are ongoing.

The incorporation of graphene nanoplatelets (GnPs) within a polymer matrix can play an important role in the physical properties and the functionality of the composite material. Composites consisting of low-density polyethylene (LDPE) and GnPs of different concentrations were developed by mixing GnPs with a molten form of the polymeric matrix. The effect of the GnPs content on the morphological, structural, and electrical properties of the composites were investigated. As shown, graphene presence and its concentration significantly modified the polymer matrix properties, a behavior that can be employed for tailoring its applicability in electrical applications. It was found that the increase of the graphene platelets concentration seems to promote the formation of graphene agglomerates, air gaps, and inhomogeneities, while higher dielectric constant/lower dielectric losses can be achieved.

The development of materials offering electromagnetic interference (EMI) shielding is of significant consideration, since this can help in expanding the lifetime of devices, electromagnetic compatibility, as well as the protection of biological systems. Conductive paints used widely today in electromagnetic interference (EMI) shielding applications are often based on organic solvents that can create safety issues due to the subsequent environment problems. This paper concerned the development of eco-friendly conductive water-based paints for use in EMI-shielding applications. Graphene nanoplatelets, polyaniline emeraldine (PANI) doped with poly(styrene sulfonic acid) (PSS) or HCl or HBr and poly(3,4-ethylenedioxythiophene) poly(styrene sulfonic acid) (PEDOT:PSS) in various ratios were employed in a water base for developing the paints. The target was to develop homogeneous water-based paint-like fluid mixtures easily applied onto surfaces using a paint brush, leading in homogeneous, uniform, opaque layers, draying fast in air at room temperature, and having quite good electrical conductivity that can offer efficient EMI-shielding performance. The results of this parametric trial indicated the optimum compositions leading in paints with optimized properties that can result in uniform, homogeneous, and conductive layers up to a thickness of over 500 μm without deformation and cracking, offering attenuation of up to 60 dBs of incoming GHz electromagnetic radiation. In addition, the structural and morphological characteristics of these paints were studied in detail.