This article presents the results of research work devoted to improving the characteristics of paint and varnish coatings based on aqueous dispersions of polyacrylates; it is proposed to modify them by introducing mineral raw materials as fillers and hydrated lime, with subsequent processing in a vortex layer apparatus. The introduction of activated diatomite does not cause the deterioration of covering power, adhesion or an increase in the porosity of the paint material. The modification of coatings contributes to an increase in their operational properties, which can be associated with a reduction in the free volume in the composite and the formation of polymer boundary layers with modified physical and chemical properties. The aim of this study is to obtain a water-dispersion paint and varnish composition containing modified diatomite on a polyacrylate basis and, subsequently, study its main physical and mechanical parameters. The work has been carried out by the following method: determination of porosity, adhesion, elasticity and covering power of the control composition; determination of porosity, adhesion, elasticity and covering power of the obtained composites using modified filler; investigation of the influence of radiation on the infrared spectrum of the paint coating surface using a FLIRB620 thermal imager. As a result of this research work, it was noticed that the modification of water dispersions with silica-activated diatomite helps to eliminate the main disadvantages of materials and coatings based on acrylate binders—low water resistance and low physical and mechanical characteristics. The introduction of modified diatomite into water-emulsion paint on an acrylate base does not lead to the deterioration of the main performance characteristics of paint coatings—porosity, adhesion, elasticity and covering.

The article presents the results of research work devoted to improving the characteristics of paint and varnish coatings based on aqueous dispersions of polyacrylates, it is proposed to modify them by introducing mineral raw materials as fillers and hydrated lime with subsequent processing in a vortex layer apparatus. Introduction of activated diatomite does not cause deterioration of covering power, adhesion and increase of porosity of the paint material. Modification of coatings contributes to the increase of their operational properties, which can be associated with the reduction of free volume in the composite, formation of polymer boundary layers with modified physical and chemical properties. The aim of the study is to obtain water-dispersion paint and varnish composition containing modified diatomite on polyacrylate basis and subsequent study of the main physical and mechanical parameters. The work has been carried out by the following method: determination of porosity, adhesion, elasticity, covering power of the control composition; determination of porosity, adhesion, elasticity, and covering power of the obtained composites using modified filler; investigation of the influence of radiation in the infrared spectrum of the paint coating surface using FLIRB620 thermal imager. As a result of research works it was noticed that modification of water dispersions with silica activated diatomite helps to eliminate the main disadvantages of materials and coatings based on acrylate binder - low water resistance and low physical and mechanical characteristics, introduction of modified diatomite into water emulsion paint on acrylate base does not lead to deterioration of the main performance characteristics of paint coatings - porosity, adhesion, elasticity and covering.

During the operation of structures, the components and materials from which they are made are exposed to various environmental, technological, and operational impacts. In this context, the use of a modified water-dispersion composition containing finely dispersed fillers with enhanced protective and performance characteristics proves to be effective. This article examines the development of a paint-and-coating composition using hollow glass microspheres and modified diatomite as finely dispersed fillers. The influence of technological factors on the properties of coating materials based on a synthesized acrylic dispersion and fillers—such as modified diatomite and hollow glass microspheres ranging from 20 to 100 μm in size with a bulk density of 0.107–0.252 g/cm³—is analyzed. The optimal formulation of the coating materials was determined to ensure the required coating quality. Experimental results demonstrate the improved strength and hardness of the coating due to the use of acrylic dispersion obtained through an emulsifier-free method and modifiers in the form of finely dispersed fillers. It has been established that the resulting samples also exhibit high adhesion to mineral and metallic substrates, along with excellent corrosion resistance. Moreover, the incorporation of acrylic dispersion contributes to increased elasticity of the coating, resulting in improved resistance to washing and abrasion. The developed protective material can be applied to a variety of surfaces, including walls, ceilings, and roofs of buildings and structures, pipelines, and many other applications. Thus, modified water-dispersion compositions based on synthesized acrylic dispersion showed the following results: resistance to sticking—5, which is the best; chemical resistance and gloss level with standard single-phase acrylic dispersion—no destruction or change in gloss. The adhesion of coatings cured under natural conditions and under the influence of UV radiation was 1 point. The developed formulations for obtaining water-dispersion paint and varnish compositions based on synthesized polymer dispersions, activated diatomite, and hollow glass microspheres, meet all the regulatory requirements for paint and varnish materials in terms of performance, and in terms of economic indicators, the cost of 1 kg of paint is 30% lower than the standard.

The article presents the results of research work devoted to the study of composite materials on polymer binder with the content of modified mineral filler - water-dispersion paint and varnish materials on acrylic polymer with modified filler - diatomite. The aim of the study is to obtain polymer-based composites with modified diatomite (water-dispersion paint on acrylic binder) with improved performance properties. Methods: determination of porosity, adhesion, elasticity, hiding power of the control composition; determination of porosity, adhesion, elasticity, hiding power of the obtained composites with the use of modified filler; investigation of the influence of radiation in the infrared radiation (IR) region of the spectrum of the paint coating surface using FLIRB620 thermal imager. As a result of work it is noticed that modification of water dispersions by silica activated diatomite promotes elimination of the main disadvantages of materials and coatings on the basis of acrylate binder - low water resistance and low physical and mechanical characteristics, introduction of modified diatomite into water emulsion paint on acrylate basis does not lead to deterioration of the main operational characteristics of paint and varnish coatings - porosity, adhesion, elasticity and covering. When analyzing the effect of emissivity in the IR region of the spectrum of the paint coating surface, a significant effect of the quantitative content of modified diatomite on the reduction of emissivity of paint coatings in the IR region of the spectrum was established and it was shown that a significant effect of the reduction of emissivity of paint coatings in the IR region of the spectrum is provided by the introduction of modified diatomite in the amount of 40 wt.h. into the mixture. The influence of the time of full-scale tests in the investigated small range regardless of the quantitative composition of modified diatomite on the performance characteristics of the paintwork was established.