Highly dense arrays of ordered and aligned nanorods of polyaniline with 10 nm diameter on transparent ITO substrate have been successfully fabricated using supramolecular assemblies of block copolymer as scaffold material; the ordered arrays of polyaniline nanorods so fabricated were found to exhibit excellent electrochemical properties with an electrochemical capacitance value of 3407 F g⁻¹.

Collision welding processes are accompanied by the ejection of a metal jet, a cloud of particles (CoP), or both phenomena, respectively. The purpose of this study is to investigate the formation, the characteristics as well as the influence of the CoP on weld formation. Impact welding experiments on three different setups in normal ambient atmosphere and under vacuum-like conditions are performed and monitored using a high-speed camera, accompanied by long-term exposures, recordings of the emission spectrum, and an evaluation of the CoP interaction with witness pins made of different materials. It was found that the CoP formed during the collision of the joining partners is compressed by the closing joining gap and particularly at small collision angles it can reach temperatures sufficient to melt the surfaces to be joined. This effect was proved using a tracer material that is detectable on the witness pins after welding. The formation of the CoP is reduced with increasing yield strength of the material and the escape of the CoP is hindered with increasing surface roughness. Both effects make welding with low-impact velocities difficult, whereas weld formation is facilitated using smooth surfaces and a reduced ambient pressure under vacuum-like conditions. Furthermore, the absence of surrounding air eases the process observation since exothermic oxidation reactions and shock compression of the gas are avoided. This also enables an estimation of the temperature in the joining gap, which was found to be more than 5600 K under normal ambient pressure.

Diffusion bonding is a well-known technology for a wide range of advanced joining applications, due to the possibility of bonding different materials within a defined temperature-time-contact pressure regime in solid state. For this study, aluminium alloys AA 6060, AA 6082, AA 7020, AA 7075 and magnesium alloy AZ 31 B are used to produce dissimilar metal joints. Titanium and silver were investigated as interlayer materials. SEM and EDXS-analysis, micro-hardness measurements and tensile testing were carried out to examine the influence of the interlayers on the diffusion zone microstructures and to characterize the joint properties. The results showed that the highest joint strength of 48 N/mm2 was reached using an aluminium alloy of the 6000 series with a titanium interlayer. For both interlayer materials, intermetallic Al-Mg compounds were still formed, but the width and the level of hardness across the diffusion zone was significantly reduced compared to Al-Mg joints without interlayer.