Hydrogels as biomaterials possess appropriate physicochemical and mechanical properties that enable the formation of a three-dimensional, stable structure used in tissue engineering and 3D printing. The integrity of the hydrogel composition is due to the presence of covalent or noncovalent cross-linking bonds. Using various cross-linking methods and agents is crucial for adjusting the properties of the hydrogel to specific biomedical applications, e.g., for direct bioprinting. The research subject was mixtures of gel-forming polymers: sodium alginate and gelatin. The polymers were cross-linked ionically with the addition of CaCl₂ solutions of various concentrations (10%, 5%, 2.5%, and 1%) and covalently using squaric acid (SQ) and dialdehyde starch (DAS). Initially, the polymer mixture’s composition and the hydrogel cross-linking procedure were determined. The obtained materials were characterized by mechanical property tests, swelling degree, FTIR, SEM, thermal analysis, and biological research. It was found that the tensile strength of hydrogels cross-linked with 1% and 2.5% CaCl₂ solutions was higher than after using a 10% solution (130 kPa and 80 kPa, respectively), and at the same time, the elongation at break increased (to 75%), and the stiffness decreased (Young Modulus is 169 kPa and 104 kPa, respectively). Moreover, lowering the concentration of the CaCl₂ solution from 10% to 1% reduced the final material’s toxicity. The hydrogels cross-linked with 1% CaCl₂ showed lower degradation temperatures and higher weight losses than those cross-linked with 2.5% CaCl₂ and therefore were less thermally stable. Additional cross-linking using SQ and DAS had only a minor effect on the strength of the hydrogels, but especially the use of 1% DAS increased the material’s elasticity. All tested hydrogels possess a 3D porous structure, with pores of irregular shape and heterogenic size, and their swelling degree initially increased sharply to the value of approx. 1000% during the first 6 h, and finally, it stabilized at a level of 1200–1600% after 24 h. The viscosity of 6% gelatin and 2% alginate solutions with and without cross-linking agents was similar, and they were only slightly shear-thinning. It was concluded that a mixture containing 2% sodium alginate and 6% gelatin presented optimal properties after gel formation and lowering the concentration of the CaCl₂ solution to 1% improved the hydrogel’s biocompatibility and positively influenced the cross-linking efficiency. Moreover, chemical cross-linking by DAS or SQ additionally improved the final hydrogel’s properties and the mixture’s printability. In conclusion, among the tested systems, the cross-linking of 6% gelatin–2% alginate mixtures by 1% DAS addition and 1% CaCl₂ solution is optimal for tissue engineering applications and potentially suitable for 3D printing.

Hydrogel materials based on sodium alginate find versatile applications in regenerative medicine and tissue engineering due to their unique properties, such as biocompatibility and biodegradability, and the possibility of the customization of their mechanical properties, such as in terms of the individual requirements of separate clinical applications. These materials, however, have numerous limitations in the area of biological activity. In order to eliminate their limitations, sodium alginate is popularly applied in combination with added gelatin, which represents a product of collagen hydrolysis. Despite numerous beneficial biological properties, matrix materials based on gelatin have poor mechanical properties and are characterized by their ability for rapid degradation in an aqueous environment, particularly at the physiological temperature of the body, which significantly limits the independent application opportunities of this type of composition in the range of scaffolding production dedicated for tissue engineering. Collagen hydrogels, unlike gelatin, are characterized by higher bioactivity, dictated by a greater number of ligands that allow for cell adhesion, as well as better stability under physiological conditions. Fish-derived collagen provides a material that may be efficiently extracted without the risk of mammalian prion infection and can be used in all patients without religious restrictions. Considering the numerous advantages of collagen indicating its superiority over gelatin, within the framework of this study, the compositions of hydrogel materials based on sodium alginate and fish collagen in different concentrations were developed. Prepared hydrogel materials were compared with the properties of a typical composition of alginate with the addition of gelatin. The rheological, mechanical, and physicochemical properties of the developed polymer compositions were evaluated. The first trials of 3D printing by extrusion technique using the analyzed polymer solutions were also conducted. The results obtained indicate that replacing gelatin with fish collagen at an analogous concentration leads to obtaining materials with a lower swelling degree, better mechanical properties, higher stability, limited release kinetics of calcium ions cross-linking the alginate matrix, a slowed process of protein release under physiological conditions, and the possibility of extrusion 3D printing. The conducted analysis highlights that the optimization of the applied concentrations of fish collagen additives to composition based on sodium alginate creates the possibility of designing materials with appropriate mechanical and rheological properties and degradation kinetics adjusted to the requirements of specific applications, leading to the prospective opportunity to produce materials capable of mimicking the properties of relevant soft tissues. Thanks to its excellent bioactivity and lower-than-gelatin viscosity of the polymer solution, fish collagen also provides a prospective solution for applications in the field of 3D bioprinting.

The common use of hydrogel materials in 3D bioprinting techniques is dictated by the unique properties of hydrogel bioinks, among which some of the most important in terms of sustaining vital cell functions in vitro in 3D cultures are the ability to retain large amounts of liquid and the ability to modify rigidity and mechanical properties to reproduce the structure of the natural extracellular matrix. Due to their high biocompatibility, non-immunogenicity, and the possibility of optimizing rheological properties and bioactivity at the same time, one of the most commonly used hydrogel bioink compositions are polymer solutions based on sodium alginate and gelatin. In 3D bioprinting techniques, it is necessary for hydrogel printouts to feature an appropriate geometry to ensure proper metabolic activity of the cells contained inside the printouts. The desired solution is to obtain a thin-walled printout geometry, ensuring uniform nutrient availability and gas exchange during cultivation. Within this study’s framework, tubular bioprinted structures were developed based on sodium alginate and gelatin, containing cells of the immortalized fibroblast line NIH/3T3 in their structure. Directly after the 3D printing process, such structures are characterized by extremely low mechanical strength. The purpose of this study was to perform a comparative analysis of the viability and spreading ability of the biological material contained in the printouts during their incubation for a period of 8 weeks while monitoring the effect of cellular growth on changes in the mechanical properties of the tubular structures. The observations demonstrated that the cells contained in the 3D printouts reach the ability to grow and spread in the polymer matrix after 4 weeks of cultivation, leading to obtaining a homogeneous, interconnected cell network inside the hydrogel after 6 weeks of incubation. Analysis of the mechanical properties of the printouts indicates that with the increasing time of cultivation of the structures, the degree of their overgrowth by the biological material contained inside, and the progressive degradation of the polymer matrix process, the tensile strength of tubular 3D printouts varies.